LG Chemical LP170L PVC
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
General Description: LP170L, homopolymer made from micro- suspension polymerization, is a medium- viscosity PVC resin with a pseudo plastic flow property in processing range. LP170L can be used for synthetic leather foam layer made by Knife coating/ Roll coating/ Gravure coating especially, products made from LP170L are excellent in restoring force and print ability.Main Applications: Slush molding, synthetic leather, gloveCAS No: 9002-86-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.406 g/cc | 1.406 g/cc | |
| Bulk Density | 0.290 – 0.390 g/cc | 0.0105 – 0.0141 lb/in³ | ASTM D1895 |
| Volatiles | <= 1.5 %
@Temperature 110 °C,
Time 3600 sec |
<= 1.5 %
@Temperature 230 °F,
Time 1.00 hour |
ASTM D3030-90 |
| Brookfield Viscosity | 2000 – 4000 cP | 2000 – 4000 cP | DOP 60phr, 6RPM; ASTM D1824-90 |
| Viscosity Measurement | >= 1.0
@Pressure 0.400 MPa
|
>= 1.0
@Pressure 58.0 psi
|
[g/sec], DOP 60phr, Severs; ASTM D1823-90 |
| Molecular Weight | 60000 – 150000 g/mol | 60000 – 150000 g/mol |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 302 °C | 576 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Autoignition Temperature | 435°C | |
| Degree of Polymerization | 1600-1700 | 30°C, JIS K6721-77 |
| K-Value | 76 | DIN53726 |