LG Chemical LUCON SP9306FL sPS+MF
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description Injection Molding Grade, sPS+MF, Low Thermal Conductivity, Chemical Resistance, High Heat ResistanceApplication: Electrical or Electronic Parts CAS No. 9003-53-6, 65997-17-3, 68928-70-1 and 1309-64-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0020 – 0.0080 cm/cm
@Thickness 3.20 mm
|
0.0020 – 0.0080 in/in
@Thickness 0.126 in
|
ASTM D955 |
| Melt Flow | 6.0 g/10 min
@Load 2.16 kg,
Temperature 290 °C |
6.0 g/10 min
@Load 4.76 lb,
Temperature 554 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 118 MPa
@Thickness 3.20 mm
|
17100 psi
@Thickness 0.126 in
|
5mm/min; ASTM D638 |
| Flexural Yield Strength | 177 MPa
@Thickness 6.40 mm
|
25600 psi
@Thickness 0.252 in
|
1.3mm/min; ASTM D790 |
| Flexural Modulus | 0.177 GPa
@Thickness 6.40 mm
|
25.6 ksi
@Thickness 0.252 in
|
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.686 J/cm
@Thickness 3.20 mm,
Temperature 23.0 °C |
1.29 ft-lb/in
@Thickness 0.126 in,
Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C
@Thickness 6.40 mm
|
500 °F
@Thickness 0.252 in
|
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C
@Thickness 6.40 mm
|
428 °F
@Thickness 0.252 in
|
ASTM D648 |
| UL RTI, Electrical | 125 °C
@Thickness >=1.60 mm
|
257 °F
@Thickness >=0.0630 in
|
|
| 130 °C
@Thickness >=3.00 mm
|
266 °F
@Thickness >=0.118 in
|
||
| UL RTI, Mechanical with Impact | 115 °C
@Thickness >=1.60 mm
|
239 °F
@Thickness >=0.0630 in
|
|
| 120 °C
@Thickness >=3.00 mm
|
248 °F
@Thickness >=0.118 in
|
||
| UL RTI, Mechanical without Impact | 125 °C
@Thickness >=1.60 mm
|
257 °F
@Thickness >=0.0630 in
|
|
| 130 °C
@Thickness >=3.00 mm
|
266 °F
@Thickness >=0.118 in
|
||
| Flammability, UL94 | V-0
@Thickness >=1.60 mm
|
V-0
@Thickness >=0.0630 in
|
|
| V-0
@Thickness >=3.00 mm
|
V-0
@Thickness >=0.118 in
|
||
| 5VA
@Thickness >=1.60 mm
|
5VA
@Thickness >=0.0630 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 – 300 °C | 500 – 572 °F | Injection Molding |
| Middle Barrel Temperature | 270 – 320 °C | 518 – 608 °F | Injection Molding |
| Front Barrel Temperature | 275 – 320 °C | 527 – 608 °F | Injection Molding |
| Nozzle Temperature | 315 °C | 599 °F | Injection Molding |
| Melt Temperature | 315 °C | 599 °F | Resin, Injection Molding |
| Mold Temperature | 80.0 – 130 °C | 176 – 266 °F | Injection Molding |
| Drying Temperature | 120 – 140 °C | 248 – 284 °F | Injection Molding |
| Dry Time | 3.00 – 5.00 hour | 3.00 – 5.00 hour | Injection Molding |
| Back Pressure | 0.981 – 3.92 MPa | 142 – 569 psi | Injection Molding |
| Screw Speed | 40 – 60 rpm | 40 – 60 rpm | Injection Molding |