LG Chemical LUSEP SP2300 SPS+GF30%, General Purpose
| Manufacturer | LG Chemical |
| Trade Name | LUSEP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Feature: Injection Molding, sPS+GF30%, General PurposeApplication: Pump Units, Pick-up Lends Holder, etc.CAS No. 9003-53-6 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0030 – 0.0090 cm/cm
@Thickness 3.20 mm
|
0.0030 – 0.0090 in/in
@Thickness 0.126 in
|
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 118 MPa
@Thickness 3.20 mm
|
17100 psi
@Thickness 0.126 in
|
5mm/min; ASTM D638 |
| Elongation at Break | 2.0 %
@Thickness 3.20 mm
|
2.0 %
@Thickness 0.126 in
|
5mm/min; ASTM D638 |
| Flexural Yield Strength | 177 MPa
@Thickness 3.20 mm
|
25600 psi
@Thickness 0.126 in
|
1.3mm/min; ASTM D790 |
| Flexural Modulus | 8.83 GPa
@Thickness 3.20 mm
|
1280 ksi
@Thickness 0.126 in
|
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm
@Thickness 3.20 mm,
Temperature 23.0 °C |
1.65 ft-lb/in
@Thickness 0.126 in,
Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C
@Thickness 6.40 mm
|
500 °F
@Thickness 0.252 in
|
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 220 °C
@Thickness 6.40 mm
|
>= 428 °F
@Thickness 0.252 in
|
Unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C
@Thickness >=1.50 mm
|
122 °F
@Thickness >=0.0591 in
|
|
| 50.0 °C
@Thickness >=3.00 mm
|
122 °F
@Thickness >=0.118 in
|
||
| UL RTI, Mechanical with Impact | 50.0 °C
@Thickness >=1.50 mm
|
122 °F
@Thickness >=0.0591 in
|
|
| 50.0 °C
@Thickness >=3.00 mm
|
122 °F
@Thickness >=0.118 in
|
||
| UL RTI, Mechanical without Impact | 50.0 °C
@Thickness >=1.50 mm
|
122 °F
@Thickness >=0.0591 in
|
|
| 50.0 °C
@Thickness >=3.00 mm
|
122 °F
@Thickness >=0.118 in
|
||
| Flammability, UL94 | HB
@Thickness >=1.50 mm
|
HB
@Thickness >=0.0591 in
|
|
| HB
@Thickness >=3.00 mm
|
HB
@Thickness >=0.118 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 35.0 kV/mm
@Thickness 1.00 mm
|
889 kV/in
@Thickness 0.0394 in
|
ASTM D149 |
| Arc Resistance | 120 – 180 sec | 120 – 180 sec | ASTM D495 |
| Comparative Tracking Index | 500 – 600 V | 500 – 600 V | Solution A; IEC 60112 |
| Hot Wire Ignition, HWI | 15 – 30 sec
@Thickness >=3.00 mm
|
15 – 30 sec
@Thickness >=0.118 in
|
|
| High Amp Arc Ignition, HAI | 30 – 60 arcs
@Thickness 3.00 mm
|
30 – 60 arcs
@Thickness 0.118 in
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 – 290 °C | 518 – 554 °F | Injection Molding |
| Middle Barrel Temperature | 280 – 310 °C | 536 – 590 °F | Injection Molding |
| Front Barrel Temperature | 290 – 310 °C | 554 – 590 °F | Injection Molding |
| Nozzle Temperature | 280 – 310 °C | 536 – 590 °F | Injection Molding |
| Melt Temperature | 280 – 310 °C | 536 – 590 °F | Injection Molding |
| Mold Temperature | 80.0 – 150 °C | 176 – 302 °F | Injection Molding |
| Drying Temperature | 80.0 – 100 °C | 176 – 212 °F | Injection Molding |
| Dry Time | 3.00 – 5.00 hour | 3.00 – 5.00 hour | Injection Molding |
| Screw Speed | 40 – 80 rpm | 40 – 80 rpm | Injection Molding |