Loxim 811 02T HB Polypropylene Compound, 10% Talc Filled, Flame Retardant
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.920 – 1.02 g/cc | 0.920 – 1.02 g/cc | ASTM D792 |
| Filler Content | 10 % | 10 % | |
| Linear Mold Shrinkage | 0.011 – 0.013 cm/cm | 0.011 – 0.013 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 28.0 – 90.0 MPa | 4060 – 13100 psi | ASTM D683 |
| Flexural Modulus | 1.60 – 1.70 GPa | 232 – 247 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 – 1.00 J/cm | 1.50 – 1.87 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 – 102 °C | 208 – 216 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|