LTL Color Compounds ColorFast® ACR100IM Polymethylmethacrylate, High Impact
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
High impact version, extrusion or injection molding PMMAAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 – 0.0060 cm/cm | 0.0020 – 0.0060 in/in | 0.125; ASTM D955 |
| Melt Flow | 1.0 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
1.0 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 45 | 45 | ASTM D785 |
| Tensile Strength, Yield | 37.9 MPa | 5500 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 35 % | 35 % | 2.0 in/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm
@Temperature 22.8 °C
|
1.10 ft-lb/in
@Temperature 73.0 °F
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 79.4 °C | 175 °F | Unannealed (0.250″); ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 – 232 °C | 410 – 450 °F | |
| Middle Barrel Temperature | 216 – 238 °C | 420 – 460 °F | |
| Front Barrel Temperature | 221 – 243 °C | 430 – 470 °F | |
| Nozzle Temperature | 216 – 238 °C | 420 – 460 °F | |
| Melt Temperature | 221 – 243 °C | 430 – 470 °F | |
| Mold Temperature | 65.6 – 87.8 °C | 150 – 190 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 – 4 hour | 3 – 4 hour | nominal; maximum drying time of 48 hours |
| Back Pressure | 0.689 – 1.38 MPa | 100 – 200 psi | |
| Shot Size | 40 – 60 % | 40 – 60 % | |
| Vent Depth | 0.00254 – 0.00762 cm | 0.00100 – 0.00300 in | |
| Screw Speed | 40 – 70 rpm | 40 – 70 rpm |