Mitsui AURUM® 450 Thermoplastic Polyimide Resin, Non-filled (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to its semicrystalline state. In addition, it displays low outgassing, superior radiation resistance and excellent chemical resistance properties.Applications: Components for automotive and aircraft enginesTransmissionFarming, off-road and construction equipmentIndustrial machineryElectric motors, pumps and compressorsBusiness machines such as laser pointers and high speed copy machinesElectronic and semiconductor transport mediaAnalytical and medical equipmentConveyors and textile equipmentInformation provided by Mitsui.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Water Absorption | 0.34 % | 0.34 % | 24 hours; ASTM D570 |
| Moisture Absorption at Equilibrium | 0.24 % | 0.24 % | 24 hours, 23°C, 60% RH |
| Linear Mold Shrinkage | 0.0083 cm/cm | 0.0083 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Hardness, Rockwell R | 129 | 129 | ASTM D785 |
| Tensile Strength at Break | 92.2 MPa | 13400 psi | ASTM D638 |
| Tensile Strength, Ultimate | 57.9 MPa
@Temperature 150 °C
|
8400 psi
@Temperature 302 °F
|
ASTM D638 |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| 90 %
@Temperature 150 °C
|
90 %
@Temperature 302 °F
|
ASTM D638 | |
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| 88.3 MPa
@Temperature 150 °C
|
12800 psi
@Temperature 302 °F
|
ASTM D790 | |
| Flexural Modulus | 2.94 GPa | 426 ksi | ASTM D790 |
| 2.55 GPa
@Temperature 150 °C
|
370 ksi
@Temperature 302 °F
|
ASTM D790 | |
| Compressive Strength | 76.5 MPa
@Temperature 150 °C
|
11100 psi
@Temperature 302 °F
|
JIS K7208 |
| 120 MPa
@Temperature 23.0 °C
|
17400 psi
@Temperature 73.4 °F
|
JIS K7208 | |
| Compressive Modulus | 1.57 GPa | 228 ksi | At 150°C; JIS K7208 |
| 2.16 GPa | 313 ksi | At 23°C; JIS K7208 | |
| Shear Strength | 78.5 MPa
@Temperature 150 °C
|
11400 psi
@Temperature 302 °F
|
JIS K7214 |
| 81.4 MPa
@Temperature 23.0 °C
|
11800 psi
@Temperature 73.4 °F
|
JIS K7214 | |
| Izod Impact, Notched | 0.883 J/cm | 1.65 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 µm/m-°C
@Temperature 23.0 °C
|
30.6 µin/in-°F
@Temperature 73.4 °F
|
MD; ASTM D696 |
| 55.0 µm/m-°C
@Temperature 200 °C
|
30.6 µin/in-°F
@Temperature 392 °F
|
MD; ASTM D696 | |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C
@Temperature 23.0 °C
|
30.6 µin/in-°F
@Temperature 73.4 °F
|
ASTM D696 |
| 55.0 µm/m-°C
@Temperature 200 °C
|
30.6 µin/in-°F
@Temperature 392 °F
|
ASTM D696 | |
| Specific Heat Capacity | 1.00 J/g-°C
@Temperature 23.0 °C
|
0.239 BTU/lb-°F
@Temperature 73.4 °F
|
By DSC |
| 1.00 J/g-°C
@Temperature 100 °C
|
0.239 BTU/lb-°F
@Temperature 212 °F
|
By DSC | |
| 1.42 J/g-°C
@Temperature 300 °C
|
0.339 BTU/lb-°F
@Temperature 572 °F
|
By DSC | |
| Thermal Conductivity | 0.174 W/m-K | 1.21 BTU-in/hr-ft²-°F | |
| Melting Point | 388 °C | 730 °F | |
| Maximum Service Temperature, Air | 238 °C | 460 °F | Heat distortion temperature, load unknown; ASTM D648 |
| Glass Transition Temp, Tg | 250 °C | 482 °F | By DSC |
| Decomposition Temperature | 570 °C | 1060 °F | 5% weight reduction temperature, by DTG |
| Flammability, UL94 | V-0
@Thickness 0.400 mm
|
V-0
@Thickness 0.0157 in
|
all color |
| 5VA
@Thickness 2.00 mm
|
5VA
@Thickness 0.0787 in
|
all color | |
| Oxygen Index | 47 %
@Thickness 3.20 mm
|
47 %
@Thickness 0.126 in
|
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 – 1.00e+18 ohm-cm | 1.00e+17 – 1.00e+18 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+17 – 1.00e+18 ohm | 1.00e+17 – 1.00e+18 ohm | ASTM D257 |
| Dielectric Constant | 3.1
@Frequency 1e+6 Hz
|
3.1
@Frequency 1e+6 Hz
|
ASTM D150 |
| 3.2
@Frequency 1000 Hz
|
3.2
@Frequency 1000 Hz
|
ASTM D150 | |
| Dissipation Factor | 0.00090
@Frequency 1000 Hz
|
0.00090
@Frequency 1000 Hz
|
ASTM D150 |
| 0.0034
@Frequency 1e+6 Hz
|
0.0034
@Frequency 1e+6 Hz
|
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 – 420 °C | 734 – 788 °F | Injection molding, extrusion |