Mitsui AURUM® PL450C Polyimide (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AURUM PL450C is a high performance thermoplastic polyimide for precision injection molded components and extruded products. A member of the AURUM family of advanced engineering resins, unfilled AURUM PL450C offers a unique balance of mechanical and thermal properties for superior performance in demanding automotive, business machinery, industrial equipment, aerospace, and semiconductor equipment applications. AURUM exhibits outstanding resistance to chemicals and radiation, a low coefficient of thermal expansion, ultrahigh purity, low outgassing in a vacuum, excellent electrical properties, and flame resistance. AURUM PL450C can be conventionally extruded to produce high performance wire & cable insulation, thin-wall tubing, and fiber.Applications: AURUM PL450C injection molded components are excellent replacements for metals, ceramics, and other plastics. High performance AURUM PL450C parts include heat-resistant gears, seals, ferrules and other fasteners, coil bobbins, semiconductor manufacturing and handling equipment components, and thermal and electrical insulators. Products produced from extruded AURUM PL450C resin include thin-wall tubing, wire and cable insulation, monofilament, and rod stock shapes.Information provided by DuPont
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Water Absorption | 0.34 % | 0.34 % | 24 hrs @ 73°F; ASTM D570 |
| Moisture Absorption at Equilibrium | 0.24 % | 0.24 % | 73°F; 60 RH, 24hrs |
| Linear Mold Shrinkage | 0.0083 cm/cm | 0.0083 in/in | ASTM D955 |
| Melt Flow | 4.5 – 7.5 g/10 min
@Load 1.05 kg,
Temperature 400 °C |
4.5 – 7.5 g/10 min
@Load 2.31 lb,
Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 92.18 MPa | 13370 psi | ASTM D638 |
| 57.9 MPa
@Temperature 149 °C
|
8400 psi
@Temperature 300 °F
|
ASTM D638 | |
| Elongation at Yield | 90 % | 90 % | ASTM D638 |
| 90 %
@Temperature 149 °C
|
90 %
@Temperature 300 °F
|
ASTM D638 | |
| Modulus of Elasticity | 2.76 GPa | 400 ksi | ASTM D882 |
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| 88.3 MPa
@Temperature 149 °C
|
12800 psi
@Temperature 300 °F
|
ASTM D790 | |
| Flexural Modulus | 2.943 GPa | 426.8 ksi | ASTM D790 |
| 2.550 GPa
@Temperature 149 °C
|
369.9 ksi
@Temperature 300 °F
|
ASTM D790 | |
| Compressive Strength | 76.5 MPa
@Temperature 149 °C
|
11100 psi
@Temperature 300 °F
|
JIS K7208 |
| 119.7 MPa
@Temperature 22.8 °C
|
17360 psi
@Temperature 73.0 °F
|
JIS K7208 | |
| Izod Impact, Notched | 0.908 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 54.0 µm/m-°C
@Temperature 22.8 °C
|
30.0 µin/in-°F
@Temperature 73.0 °F
|
MD; ASTM D696 |
| 54.0 µm/m-°C
@Temperature 73.0 °C
|
30.0 µin/in-°F
@Temperature 163 °F
|
TD; ASTM D696 | |
| Specific Heat Capacity | 1.00 J/g-°C | 0.240 BTU/lb-°F | DSC |
| 1.004 J/g-°C
@Temperature 100 °C
|
0.2400 BTU/lb-°F
@Temperature 212 °F
|
DSC | |
| 1.423 J/g-°C
@Temperature 300 °C
|
0.3400 BTU/lb-°F
@Temperature 572 °F
|
DSC | |
| Thermal Conductivity | 0.174333 W/m-K | 1.20987 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 388 °C | 730 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 238 °C | 460 °F | ASTM D648 |
| Glass Transition Temp, Tg | 250 °C | 482 °F | DSC |
| Flammability, UL94 | V-0
@Thickness 0.400 mm
|
V-0
@Thickness 0.0157 in
|
|
| 5VA
@Thickness 2.00 mm
|
5VA
@Thickness 0.0787 in
|
||
| Oxygen Index | 47 %
@Thickness 3.20 mm
|
47 %
@Thickness 0.126 in
|
ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 – 1.00e+18 ohm-cm | 1.00e+17 – 1.00e+18 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+17 – 1.00e+18 ohm | 1.00e+17 – 1.00e+18 ohm | ASTM D257 |
| Dielectric Constant | 3.1
@Frequency 1e+6 Hz
|
3.1
@Frequency 1e+6 Hz
|
ASTM D150 |
| 3.2
@Frequency 1000 Hz
|
3.2
@Frequency 1000 Hz
|
ASTM D150 | |
| Dissipation Factor | 0.00090
@Frequency 1000 Hz
|
0.00090
@Frequency 1000 Hz
|
ASTM D150 |
| 0.0034
@Frequency 1e+6 Hz
|
0.0034
@Frequency 1e+6 Hz
|
ASTM D150 |