Multibase TPSiV™ 3011-50A Thermoplastic Silicone Vulcanizate
| Manufacturer | Multibase |
| Trade Name | TPSiV™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
These materials are a novel family of TPV products based on cross-linked silicone rubber dispersed into various engineering thermoplastics. The dispersion of the silicone internal phase is produced by dynamic “vulcanization” or cross-linking of silicone polymers within the thermoplastic organic phase and results in a stable droplet type morphology as shown in the TEM micrograph. TPSiV™ combines the elastomeric performance of silicone rubber with the melt re-processability and thermal and chemical resistance of engineering thermoplastics.Thermoplastic polyurethane based TPSiV™ (3010, 3011, 3111, 3040, 3340 grades) combine the benefits of excellent abrasion resistance from the polyurethane as well as the lower coefficient of friction and improved temperature properties from the silicone rubber.TPSiV™ 3011-50A / 60A / 70A / 85A: General purpose grades designed for both injection molding and extrusion applications. Plasticizer free (except the 50A product), which results in excellent bonding via 2-shot molding or co-extrusion to PC, ABS, PU, and PVC. They display good tensile and tear strength.Information provided by Multibase, a Dow Corning Company
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 58 | 58 | 10 sec; ASTM D2240 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D412 |
| Elongation at Break | 680 % | 680 % | ASTM D412 |
| Tear Strength | 40.3 kN/m | 230 pli | ASTM D412 |
| Taber Abrasion, mg/1000 Cycles | 60 | 60 | ASTM D1044 |
| Compression Set | 18 %
@Temperature 22.8 °C,
Time 79200 sec |
18 %
@Temperature 73.0 °F,
Time 22.0 hour |
|
| 84 %
@Temperature 120 °C,
Time 79200 sec |
84 %
@Temperature 248 °F,
Time 22.0 hour |
||
| Tensile Set | 10 % | 10 % | 1; ASTM D412 |
| 34 % | 34 % | 3; ASTM D412 | |
| 60 % | 60 % | At Break; ASTM D412 | |
| 60 % | 60 % | ASTM D412 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 °C | 356 °F | |
| Middle Barrel Temperature | 190 °C | 374 °F | |
| Front Barrel Temperature | 200 °C | 392 °F | |
| Nozzle Temperature | 205 °C | 401 °F | |
| Mold Temperature | 10.0 – 30.0 °C | 50.0 – 86.0 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 – 4 hour | 2 – 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Rate | Fast |