North Wood Plastics PS with 40% Wood Fiber
| Manufacturer | North Wood Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Data provided by North Wood Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.156 g/cc | 0.04176 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.00080 cm/cm | 0.00080 in/in | ASTM D955 |
| Melt Flow | 0.50 g/10 min
@Temperature 190 °C
|
0.50 g/10 min
@Temperature 374 °F
|
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Tensile Modulus | 5.80 GPa | 841 ksi | ASTM D638 |
| Flexural Yield Strength | 56.0 MPa | 8120 psi | ASTM D790 |
| Flexural Modulus | 5.20 GPa | 754 ksi | ASTM D790 |
| Izod Impact, Notched | 0.200 J/cm | 0.375 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 36.0 µm/m-°C
@Temperature 20.0 °C
|
20.0 µin/in-°F
@Temperature 68.0 °F
|
|
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 200 °C | <= 392 °F | To prevent fiber degradation. |