NOVA Chemicals Dylark® 378P30 Glass Reinforced Engineering Resin
| Manufacturer | NOVA Chemicals |
| Trade Name | Dylark® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Features: Ultra high modulus, High heat resistance, excellent adhesion to urethaneApplications: Instrument panel substrates, Brackets, Structural components
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ISO 1183 |
| Filler Content | 30 % | 30 % | Glass Fiber; ISO 3451-1 |
| Linear Mold Shrinkage | 0.0015 – 0.0035 cm/cm | 0.0015 – 0.0035 in/in | ISO 2577 |
| Melt Flow | 0.20 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
0.20 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 90.0 MPa | 13100 psi | ISO 527-2 |
| Elongation at Yield | 1.7 % | 1.7 % | ISO 527-2 |
| Tensile Modulus | 8.20 GPa | 1190 ksi | ISO 527-2 |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.70 kJ/m²
@Temperature -40.0 °C
|
4.62 ft-lb/in²
@Temperature -40.0 °F
|
ISO 180/1A |
| 9.80 kJ/m²
@Temperature 23.0 °C
|
4.66 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/1A | |
| Charpy Impact Unnotched | 2.94 J/cm² | 14.0 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.12 J/cm² | 5.33 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 43.2 µm/m-°C | 24.0 µin/in-°F | NOVA Chemicals Laboratory Procedure |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C
@Thickness 4.00 mm
|
255 °F
@Thickness 0.157 in
|
Unannealed; ISO 75-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 249 – 288 °C | 480 – 550 °F | Profile temperatures |
| Melt Temperature | 260 – 288 °C | 500 – 550 °F | Air purge at equilibrium conditions |
| Mold Temperature | 43.3 – 60.0 °C | 110 – 140 °F | Core mold surface temperature at equilibrium conditions |
| 54.4 – 71.1 °C | 130 – 160 °F | Cavity mold surface temperature at equilibrium conditions | |
| Back Pressure | 0.345 – 0.689 MPa | 50.0 – 100 psi | |
| Screw Speed | 80 – 125 rpm | 80 – 125 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | medium-fast |