NOVA Chemicals Dylark® FG2500 High-Heat Styrenic Copolymer
| Manufacturer | NOVA Chemicals |
| Trade Name | Dylark® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Product Description and Features: Styrenic copolymer with high-heat resistance, high-impact strength and good toughness. Resins used in food grade sheet extrusion and injection molding applications. Microwavable ResinProcessing: Contact NOVA Chemicals technical personnel for processing assistance. Data presented here is based on test results from a limited number of samples and may change as additional manufacturing data is obtained.Availability: Available in boxes, truckloads, and railcars.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 – 0.0070 cm/cm | 0.0040 – 0.0070 in/in | ASTM D 955 |
| Melt Flow | 0.60 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
0.60 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 26.0 MPa | 3770 psi | 0.2 inches/minute; ASTM D 638 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 0.2 inches/minute; ASTM D 638 |
| Elongation at Break | 20 % | 20 % | 0.2 inches/minute; ASTM D 638 |
| Tensile Modulus | 2.07 GPa | 300 ksi | 0.2 inches/minute; ASTM D 638 |
| Flexural Strength | 57.0 MPa | 8270 psi | at <5% Strain, flexural testing speed of 0.5 inches/minute; ASTM D 790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | Flexural testing speed of 0.5 inches/minute; ASTM D 790 |
| Izod Impact, Notched | 2.67 J/cm
@Thickness 3.17 mm
|
5.00 ft-lb/in
@Thickness 0.125 in
|
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C
@Thickness 3.17 mm
|
225 °F
@Thickness 0.125 in
|
Annealed; ASTM D 648 |
| Vicat Softening Point | 123 °C
@Load 1.00 kg
|
253 °F
@Load 2.20 lb
|
Rate B; 120°C/min; ASTM D 1525 |