NOVA Chemicals Sclair® 14B3 Butene LMDPE Film Resin (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Film Properties. Features: Low gel, good clarity, heat resistance and barrier properties.Applications: Lamination, co-extrusion.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in³ | ASTM D792 |
| Melt Flow | 1.8 g/10 min
@Load 2.16 kg,
Temperature 190 °C |
1.8 g/10 min
@Load 4.76 lb,
Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| Film Elongation at Break, MD | 750 % | 750 % | ASTM D882 |
| Film Elongation at Break, TD | 950 % | 950 % | ASTM D882 |
| Secant Modulus, MD | 0.340 GPa | 49.3 ksi | ASTM D882 |
| Secant Modulus, TD | 0.370 GPa | 53.7 ksi | ASTM D882 |
| Coefficient of Friction | 0.40 | 0.40 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 1.00 g/micron | 25.4 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 5.00 g/micron | 127 g/mil | ASTM D1922 |
| Dart Drop | 1.00 g/micron | 25.4 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 38.0 MPa | 5510 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 111 °C | 232 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 15 %
@Thickness 0.0250 mm
|
15 %
@Thickness 0.000984 in
|
ASTM D1003 |
| Gloss | 58 % | 58 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 225 – 235 °C | 437 – 455 °F |