This property data is a summary of similar materials in the MatWeb database for the category “Acrylic, Extruded”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 – 1.19 g/cc | 0.0408 – 0.0430 lb/in³ | Average value: 1.18 g/cc Grade Count:37 |
| Water Absorption | 0.200 – 2.00 % | 0.200 – 2.00 % | Average value: 0.663 % Grade Count:23 |
| Moisture Absorption at Equilibrium | 0.300 – 0.360 % | 0.300 – 0.360 % | Average value: 0.312 % Grade Count:5 |
| Water Absorption at Saturation | 0.300 – 2.10 % | 0.300 – 2.10 % | Average value: 1.70 % Grade Count:9 |
| Moisture Expansion | 0.500 – 0.800 % | 0.500 – 0.800 % | Average value: 0.583 % Grade Count:6 |
| Moisture Vapor Transmission | 55.0 – 56.0 cc-mm/m²-24hr-atm | 140 – 142 cc-mil/100 in²-24hr-atm | Average value: 55.3 cc-mm/m²-24hr-atm Grade Count:3 |
| Linear Mold Shrinkage | 0.00200 – 0.00800 cm/cm | 0.00200 – 0.00800 in/in | Average value: 0.00468 cm/cm Grade Count:11 |
| Melt Flow | 0.500 – 7.00 g/10 min | 0.500 – 7.00 g/10 min | Average value: 2.16 g/10 min Grade Count:23 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 45.0 – 101 | 45.0 – 101 | Average value: 79.9 Grade Count:18 |
| Ball Indentation Hardness | 100 – 175 MPa | 14500 – 25400 psi | Average value: 149 MPa Grade Count:8 |
| Tensile Strength, Ultimate | 29.0 – 75.0 MPa | 4210 – 10900 psi | Average value: 58.4 MPa Grade Count:31 |
| 35.0 – 100 MPa
@Temperature -40.0 – 70.0 °C
|
5080 – 14500 psi
@Temperature -40.0 – 158 °F
|
Average value: 67.5 MPa Grade Count:4 | |
| Tensile Strength, Yield | 45.0 – 86.0 MPa | 6530 – 12500 psi | Average value: 73.7 MPa Grade Count:5 |
| Elongation at Break | 3.50 – 59.0 % | 3.50 – 59.0 % | Average value: 16.1 % Grade Count:29 |
| Elongation at Yield | 4.00 – 6.00 % | 4.00 – 6.00 % | Average value: 5.25 % Grade Count:4 |
| Modulus of Elasticity | 1.80 – 3.30 GPa | 261 – 479 ksi | Average value: 2.96 GPa Grade Count:19 |
| Flexural Yield Strength | 38.0 – 142 MPa | 5510 – 20600 psi | Average value: 92.7 MPa Grade Count:29 |
| Flexural Modulus | 1.20 – 3.38 GPa | 174 – 490 ksi | Average value: 2.60 GPa Grade Count:18 |
| Compressive Yield Strength | 103 MPa | 14900 psi | Average value: 103 MPa Grade Count:4 |
| Poissons Ratio | 0.370 – 0.430 | 0.370 – 0.430 | Average value: 0.402 Grade Count:6 |
| Fatigue Strength | 38.0 MPa | 5510 psi | Average value: 38.0 MPa Grade Count:3 |
| Shear Modulus | 0.629 – 1.70 GPa | 91.2 – 247 ksi | Average value: 1.08 GPa Grade Count:6 |
| Izod Impact, Notched | 0.147 – 0.588 J/cm | 0.275 – 1.10 ft-lb/in | Average value: 0.309 J/cm Grade Count:10 |
| Izod Impact, Notched (ISO) | 1.60 – 8.10 kJ/m² | 0.761 – 3.85 ft-lb/in² | Average value: 4.20 kJ/m² Grade Count:15 |
| Charpy Impact Unnotched | 1.00 J/cm² – NB | 4.76 ft-lb/in² – NB | Average value: 3.90 J/cm² Grade Count:21 |
| Charpy Impact, Notched | 0.200 – 6.40 J/cm² | 0.952 – 30.5 ft-lb/in² | Average value: 0.846 J/cm² Grade Count:16 |
| Falling Dart Impact | 10.8 – 20.6 J | 8.00 – 15.2 ft-lb | Average value: 14.9 J Grade Count:3 |
| Coefficient of Friction | 0.450 – 0.800 | 0.450 – 0.800 | Average value: 0.583 Grade Count:3 |
| Tensile Creep Modulus, 1 hour | 1400 – 2700 MPa | 203000 – 392000 psi | Average value: 2350 MPa Grade Count:4 |
| Tensile Creep Modulus, 1000 hours | 1000 – 1800 MPa | 145000 – 261000 psi | Average value: 1580 MPa Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 – 110 µm/m-°C | 33.3 – 61.1 µin/in-°F | Average value: 73.5 µm/m-°C Grade Count:20 |
| 72.0 – 72.0 µm/m-°C
@Temperature 0.000 – 156 °C
|
40.0 – 40.0 µin/in-°F
@Temperature 32.0 – 312 °F
|
Average value: 72.0 µm/m-°C Grade Count:1 | |
| Specific Heat Capacity | 1.47 J/g-°C | 0.351 BTU/lb-°F | Average value: 1.47 J/g-°C Grade Count:8 |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | Average value: 0.190 W/m-K Grade Count:4 |
| Maximum Service Temperature, Air | 65.0 – 180 °C | 149 – 356 °F | Average value: 98.9 °C Grade Count:10 |
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 – 101 °C | 178 – 214 °F | Average value: 94.2 °C Grade Count:19 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 – 103 °C | 140 – 217 °F | Average value: 88.3 °C Grade Count:24 |
| Vicat Softening Point | 66.0 – 113 °C | 151 – 235 °F | Average value: 97.4 °C Grade Count:34 |
| Glass Transition Temp, Tg | 105 – 110 °C | 221 – 230 °F | Average value: 107 °C Grade Count:3 |
| Flammability, UL94 | HB | HB | Grade Count:11 |
| Flash Point | 430 °C | 806 °F | Average value: 430 °C Grade Count:4 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 – 1.49 | 1.49 – 1.49 | Average value: 1.49 Grade Count:20 |
| Haze | 0.200 – 3.00 % | 0.200 – 3.00 % | Average value: 1.10 % Grade Count:10 |
| Transmission, Visible | 50.0 – 93.0 % | 50.0 – 93.0 % | Average value: 77.9 % Grade Count:31 |
| UV Transmittance | 0.000 – 80.0 % | 0.000 – 80.0 % | Average value: 10.3 % Grade Count:8 |
| Reflection Coefficient, Visible (0-1) | 0.0330 – 0.0400 | 0.0330 – 0.0400 | Average value: 0.0391 Grade Count:8 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+14 – 1.00e+15 ohm-cm | 1.00e+14 – 1.00e+15 ohm-cm | Average value: 7.60e+14 ohm-cm Grade Count:15 |
| Surface Resistance | 1.00e+12 – 1.00e+14 ohm | 1.00e+12 – 1.00e+14 ohm | Average value: 8.08e+13 ohm Grade Count:13 |
| Shielding Effectiveness | 26.0 – 33.0 dB | 26.0 – 33.0 dB | Average value: 30.7 dB Grade Count:5 |
| Dielectric Constant | 2.80 – 4.00 | 2.80 – 4.00 | Average value: 3.39 Grade Count:11 |
| Dielectric Strength | 15.0 – 60.0 kV/mm | 381 – 1520 kV/in | Average value: 25.7 kV/mm Grade Count:13 |
| Dissipation Factor | 0.0300 – 0.0600 | 0.0300 – 0.0600 | Average value: 0.0445 Grade Count:11 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:8 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 70.0 – 270 °C | 158 – 518 °F | Average value: 135 °C Grade Count:9 |
| Nozzle Temperature | 220 – 245 °C | 428 – 473 °F | Average value: 233 °C Grade Count:3 |
| Adapter Temperature | 230 – 240 °C | 446 – 464 °F | Average value: 235 °C Grade Count:3 |
| Die Temperature | 220 – 240 °C | 428 – 464 °F | Average value: 230 °C Grade Count:3 |
| Melt Temperature | 150 – 249 °C | 302 – 480 °F | Average value: 218 °C Grade Count:5 |
| Mold Temperature | 32.2 – 90.0 °C | 90.0 – 194 °F | Average value: 64.5 °C Grade Count:7 |