Overview of materials for Epoxy, Molded, Glass Fiber Filler
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Epoxy, Molded, Glass Fiber Filler”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 – 2.20 g/cc | 0.0361 – 0.0795 lb/in³ | Average value: 1.76 g/cc Grade Count:71 |
| Apparent Bulk Density | 0.0800 – 1.15 g/cc | 0.00289 – 0.0415 lb/in³ | Average value: 0.818 g/cc Grade Count:16 |
| Water Absorption | 0.100 – 0.500 % | 0.100 – 0.500 % | Average value: 0.175 % Grade Count:21 |
| 0.150 – 0.900 %
@Temperature 50.0 – 50.0 °C
|
0.150 – 0.900 %
@Temperature 122 – 122 °F
|
Average value: 0.244 % Grade Count:14 | |
| 0.150 – 0.900 %
@Time 173000 – 173000 sec
|
0.150 – 0.900 %
@Time 48.0 – 48.0 hour
|
Average value: 0.244 % Grade Count:14 | |
| Viscosity | 325 – 1300 cP | 325 – 1300 cP | Average value: 816 cP Grade Count:9 |
| Linear Mold Shrinkage | 0.00100 – 0.00600 cm/cm | 0.00100 – 0.00600 in/in | Average value: 0.00291 cm/cm Grade Count:35 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Barcol | 63.0 – 73.0 | 63.0 – 73.0 | Average value: 70.2 Grade Count:9 |
| Hardness, Rockwell M | 98.0 – 105 | 98.0 – 105 | Average value: 103 Grade Count:3 |
| Hardness, Shore D | 85.0 – 89.0 | 85.0 – 89.0 | Average value: 87.6 Grade Count:9 |
| Tensile Strength, Ultimate | 48.0 – 550 MPa | 6960 – 79800 psi | Average value: 180 MPa Grade Count:56 |
| Tensile Strength, Yield | 30.0 – 80.0 MPa | 4350 – 11600 psi | Average value: 58.1 MPa Grade Count:8 |
| Elongation at Break | 0.600 – 2.04 % | 0.600 – 2.04 % | Average value: 1.57 % Grade Count:15 |
| Modulus of Elasticity | 6.00 – 30.0 GPa | 870 – 4350 ksi | Average value: 16.4 GPa Grade Count:31 |
| Flexural Yield Strength | 70.0 – 1200 MPa | 10200 – 174000 psi | Average value: 267 MPa Grade Count:67 |
| >= 160 MPa
@Temperature 150 – 150 °C
|
>= 23200 psi
@Temperature 302 – 302 °F
|
Average value: 166 MPa Grade Count:5 | |
| Flexural Modulus | 6.60 – 35.0 GPa | 957 – 5080 ksi | Average value: 18.0 GPa Grade Count:54 |
| Compressive Yield Strength | 120 – 1000 MPa | 17400 – 145000 psi | Average value: 292 MPa Grade Count:57 |
| Compressive Modulus | 7.60 – 16.7 GPa | 1100 – 2420 ksi | Average value: 10.7 GPa Grade Count:5 |
| Shear Strength | 20.0 – 74.0 MPa | 2900 – 10700 psi | Average value: 39.9 MPa Grade Count:15 |
| Izod Impact, Notched | 0.200 – 24.0 J/cm | 0.375 – 45.0 ft-lb/in | Average value: 3.02 J/cm Grade Count:24 |
| Izod Impact, Notched (ISO) | 60.0 – 80.0 kJ/m² | 28.6 – 38.1 ft-lb/in² | Average value: 66.7 kJ/m² Grade Count:6 |
| Izod Impact, Unnotched (ISO) | 34.0 – 54.0 kJ/m² | 16.2 – 25.7 ft-lb/in² | Average value: 45.1 kJ/m² Grade Count:9 |
| Charpy Impact Unnotched | 0.400 – 6.00 J/cm² | 1.90 – 28.6 ft-lb/in² | Average value: 2.56 J/cm² Grade Count:22 |
| Charpy Impact, Notched | 0.150 – 0.800 J/cm² | 0.714 – 3.81 ft-lb/in² | Average value: 0.405 J/cm² Grade Count:11 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 3.60 – 47.0 µm/m-°C | 2.00 – 26.1 µin/in-°F | Average value: 24.7 µm/m-°C Grade Count:19 |
| 10.0 – 77.4 µm/m-°C
@Temperature 37.8 – 150 °C
|
5.56 – 43.0 µin/in-°F
@Temperature 100 – 302 °F
|
Average value: 33.3 µm/m-°C Grade Count:11 | |
| Thermal Conductivity | 0.277 – 0.800 W/m-K | 1.92 – 5.55 BTU-in/hr-ft²-°F | Average value: 0.540 W/m-K Grade Count:16 |
| Maximum Service Temperature, Air | 130 – 250 °C | 266 – 482 °F | Average value: 163 °C Grade Count:8 |
| Maximum Service Temperature, Inert | 140 – 200 °C | 284 – 392 °F | Average value: 168 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Average value: 200 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 – 282 °C | 230 – 540 °F | Average value: 237 °C Grade Count:35 |
| Deflection Temperature at 8.0 MPa | 100 – 200 °C | 212 – 392 °F | Average value: 163 °C Grade Count:11 |
| Glass Transition Temp, Tg | 60.0 – 170 °C | 140 – 338 °F | Average value: 97.6 °C Grade Count:12 |
| Flammability, UL94 | HB – V-0 | HB – V-0 | Grade Count:24 |
| Oxygen Index | 33.5 – 50.0 % | 33.5 – 50.0 % | Average value: 42.9 % Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+12 – 1.00e+16 ohm-cm | 1.00e+12 – 1.00e+16 ohm-cm | Average value: 2.68e+15 ohm-cm Grade Count:12 |
| Surface Resistance | 1.00e+13 – 1.00e+15 ohm | 1.00e+13 – 1.00e+15 ohm | Average value: 5.41e+14 ohm Grade Count:15 |
| Insulation Resistance | 5.00e+7 – 5.00e+11 ohm | 5.00e+7 – 5.00e+11 ohm | Average value: 1.47e+11 ohm Grade Count:20 |
| Dielectric Constant | 1.80 – 7.00 | 1.80 – 7.00 | Average value: 4.90 Grade Count:49 |
| Dielectric Strength | 0.984 – 40.0 kV/mm | 25.0 – 1020 kV/in | Average value: 15.1 kV/mm Grade Count:41 |
| Dielectric Breakdown | >= 35000 V
@Temperature 90.0 – 90.0 °C
|
>= 35000 V
@Temperature 194 – 194 °F
|
Average value: 32900 V Grade Count:9 |
| >= 10000 V
@Temperature 90.0 – 90.0 °C
|
>= 10000 V
@Temperature 194 – 194 °F
|
Average value: 32900 V Grade Count:5 | |
| >= 10000 V
@Time 20.0 – 60.0 sec
|
>= 10000 V
@Time 0.00556 – 0.0167 hour
|
Average value: 32900 V Grade Count:5 | |
| Dissipation Factor | 0.00500 – 0.0500 | 0.00500 – 0.0500 | Average value: 0.0245 Grade Count:49 |
| Arc Resistance | 120 – 240 sec | 120 – 240 sec | Average value: 172 sec Grade Count:24 |
| Comparative Tracking Index | 180 – 600 V | 180 – 600 V | Average value: 280 V Grade Count:28 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 150 – 175 °C | 302 – 347 °F | Average value: 163 °C Grade Count:3 |
| Melt Temperature | 40.0 – 110 °C | 104 – 230 °F | Average value: 76.5 °C Grade Count:5 |
| Mold Temperature | 143 – 190 °C | 289 – 374 °F | Average value: 172 °C Grade Count:9 |
| Pot Life | 20.0 – 120 min | 20.0 – 120 min | Average value: 92.2 min Grade Count:9 |