Overview of materials for Ionomer, Film Grade
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Ionomer, Film Grade”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 – 0.950 g/cc | 0.0340 – 0.0343 lb/in³ | Average value: 0.941 g/cc Grade Count:27 |
| Melt Flow | 0.700 – 14.0 g/10 min | 0.700 – 14.0 g/10 min | Average value: 3.43 g/10 min Grade Count:27 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 300 – 500 % | 300 – 500 % | Average value: 388 % Grade Count:17 |
| Film Elongation at Break, TD | 300 – 475 % | 300 – 475 % | Average value: 398 % Grade Count:17 |
| Secant Modulus, MD | 0.0500 – 0.290 GPa | 7.25 – 42.1 ksi | Average value: 0.212 GPa Grade Count:17 |
| Secant Modulus, TD | 0.0450 GPa | 6.53 ksi | Average value: 0.0450 GPa Grade Count:17 |
| Elmendorf Tear Strength, MD | 0.300 – 8.30 g/micron | 7.62 – 211 g/mil | Average value: 2.01 g/micron Grade Count:17 |
| Elmendorf Tear Strength, TD | 0.300 – 11.0 g/micron | 7.62 – 279 g/mil | Average value: 2.27 g/micron Grade Count:17 |
| Dart Drop | 6.00 – 22.1 g/micron | 152 – 561 g/mil | Average value: 10.3 g/micron Grade Count:16 |
| Seal Strength | 2000 – 3400 g/25 mm | 2000 – 3400 g/in | Average value: 2530 g/25 mm Grade Count:21 |
| Hot Tack Strength | 1800 – 3000 g/25 mm | 1800 – 3000 g/in | Average value: 2200 g/25 mm Grade Count:21 |
| Film Tensile Strength at Break, MD | 24.0 – 41.0 MPa | 3480 – 5950 psi | Average value: 32.0 MPa Grade Count:17 |
| Film Tensile Strength at Break, TD | 26.5 – 40.7 MPa | 3840 – 5900 psi | Average value: 33.8 MPa Grade Count:17 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 51.0 – 101 °C | 124 – 214 °F | Average value: 90.3 °C Grade Count:27 |
| Vicat Softening Point | 56.0 – 79.0 °C | 133 – 174 °F | Average value: 70.1 °C Grade Count:27 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.30 – 11.5 % | 1.30 – 11.5 % | Average value: 4.30 % Grade Count:17 |
| Gloss | 20.0 – 104 % | 20.0 – 104 % | Average value: 60.3 % Grade Count:17 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 260 – 285 °C | 500 – 545 °F | Average value: 280 °C Grade Count:5 |
| Adapter Temperature | 185 – 235 °C | 365 – 455 °F | Average value: 205 °C Grade Count:5 |
| Die Temperature | 185 – 235 °C | 365 – 455 °F | Average value: 205 °C Grade Count:5 |
| Melt Temperature | 160 – 304 °C | 320 – 579 °F | Average value: 200 °C Grade Count:27 |