Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Liquid Crystal Polymer (LCP), 20% Glass Fiber Filled”. Specific grades with glass content between 15% and 24% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 – 1.85 g/cc | 0.0527 – 0.0668 lb/in³ | Average value: 1.55 g/cc Grade Count:11 |
| Filler Content | 15.0 – 20.0 % | 15.0 – 20.0 % | Average value: 18.8 % Grade Count:4 |
| Linear Mold Shrinkage | -0.00200 – 0.00400 cm/cm | -0.00200 – 0.00400 in/in | Average value: 0.00159 cm/cm Grade Count:11 |
| Linear Mold Shrinkage, Transverse | 0.00200 – 0.00900 cm/cm | 0.00200 – 0.00900 in/in | Average value: 0.00557 cm/cm Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 43.0 – 80.0 | 43.0 – 80.0 | Average value: 66.5 Grade Count:4 |
| Tensile Strength, Ultimate | 100 – 200 MPa | 14500 – 29000 psi | Average value: 162 MPa Grade Count:12 |
| Elongation at Break | 1.20 – 4.50 % | 1.20 – 4.50 % | Average value: 2.76 % Grade Count:11 |
| Modulus of Elasticity | 10.5 – 16.5 GPa | 1520 – 2400 ksi | Average value: 12.8 GPa Grade Count:11 |
| Flexural Yield Strength | 133 – 250 MPa | 19300 – 36300 psi | Average value: 194 MPa Grade Count:11 |
| Flexural Modulus | 10.5 – 14.5 GPa | 1520 – 2100 ksi | Average value: 11.9 GPa Grade Count:12 |
| Compressive Yield Strength | 61.0 – 85.0 MPa | 8850 – 12300 psi | Average value: 78.3 MPa Grade Count:4 |
| Compressive Modulus | 9.50 – 11.0 GPa | 1380 – 1600 ksi | Average value: 10.1 GPa Grade Count:4 |
| Izod Impact, Notched | 1.17 – 1.87 J/cm | 2.20 – 3.50 ft-lb/in | Average value: 1.49 J/cm Grade Count:4 |
| Izod Impact, Unnotched | 4.81 – 6.94 J/cm | 9.00 – 13.0 ft-lb/in | Average value: 5.61 J/cm Grade Count:4 |
| Izod Impact, Notched (ISO) | 2.00 – 126 kJ/m² | 0.952 – 60.0 ft-lb/in² | Average value: 54.0 kJ/m² Grade Count:7 |
| Charpy Impact Unnotched | 2.50 – 10.0 J/cm² | 11.9 – 47.6 ft-lb/in² | Average value: 5.53 J/cm² Grade Count:4 |
| Charpy Impact, Notched | 0.300 – 5.90 J/cm² | 1.43 – 28.1 ft-lb/in² | Average value: 3.52 J/cm² Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | -3.00 – 23.0 µm/m-°C | -1.67 – 12.8 µin/in-°F | Average value: 6.17 µm/m-°C Grade Count:5 |
| CTE, linear, Transverse to Flow | 18.0 – 66.0 µm/m-°C | 10.0 – 36.7 µin/in-°F | Average value: 39.7 µm/m-°C Grade Count:5 |
| Melting Point | 280 – 335 °C | 536 – 635 °F | Average value: 303 °C Grade Count:8 |
| Deflection Temperature at 0.46 MPa (66 psi) | 232 – 298 °C | 450 – 568 °F | Average value: 255 °C Grade Count:5 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 – 304 °C | 365 – 580 °F | Average value: 242 °C Grade Count:12 |
| Deflection Temperature at 8.0 MPa | 103 – 157 °C | 217 – 315 °F | Average value: 134 °C Grade Count:4 |
| Vicat Softening Point | 149 – 202 °C | 300 – 396 °F | Average value: 171 °C Grade Count:5 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:9 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+12 – 1.00e+16 ohm-cm | 1.00e+12 – 1.00e+16 ohm-cm | Average value: 2.33e+15 ohm-cm Grade Count:6 |
| Surface Resistance | 1.00e+15 – 1.00e+17 ohm | 1.00e+15 – 1.00e+17 ohm | Average value: 1.75e+16 ohm Grade Count:6 |
| Dielectric Constant | 2.50 – 4.20 | 2.50 – 4.20 | Average value: 3.41 Grade Count:8 |
| Dielectric Strength | 25.6 – 40.0 kV/mm | 650 – 1020 kV/in | Average value: 33.3 kV/mm Grade Count:6 |
| Dissipation Factor | 0.00600 – 50.0 | 0.00600 – 50.0 | Average value: 5.73 Grade Count:8 |
| Arc Resistance | 135 – 145 sec | 135 – 145 sec | Average value: 138 sec Grade Count:4 |
| Comparative Tracking Index | 150 – 200 V | 150 – 200 V | Average value: 185 V Grade Count:5 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 – 345 °C | 176 – 653 °F | Average value: 190 °C Grade Count:5 |
| Die Temperature | 290 – 350 °C | 554 – 662 °F | Average value: 314 °C Grade Count:5 |
| Melt Temperature | 20.0 – 399 °C | 68.0 – 750 °F | Average value: 276 °C Grade Count:11 |
| Mold Temperature | 37.8 – 121 °C | 100 – 250 °F | Average value: 81.2 °C Grade Count:10 |
| Injection Velocity | 150 mm/sec | 5.91 in/sec | Average value: 150 mm/sec Grade Count:4 |
| Drying Temperature | 149 – 150 °C | 300 – 302 °F | Average value: 150 °C Grade Count:9 |
| Moisture Content | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:5 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:3 |
| Injection Pressure | 34.5 – 150 MPa | 5000 – 21800 psi | Average value: 95.8 MPa Grade Count:9 |