Overview of materials for Polyaryletherketone (PAEK), Glass Fiber Filled
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polyaryletherketone (PAEK), Glass Fiber Filled”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 – 1.65 g/cc | 0.0495 – 0.0596 lb/in³ | Average value: 1.53 g/cc Grade Count:11 |
| Filler Content | 30.0 – 40.0 % | 30.0 – 40.0 % | Average value: 32.0 % Grade Count:5 |
| Water Absorption | 0.0500 – 0.200 % | 0.0500 – 0.200 % | Average value: 0.122 % Grade Count:10 |
| Viscosity | 60000 – 650000 cP
@Temperature 400 – 400 °C
|
60000 – 650000 cP
@Temperature 752 – 752 °F
|
Average value: 396000 cP Grade Count:5 |
| 60000 – 650000 cP
@Shear Rate 1000 – 1000 1/s
|
60000 – 650000 cP
@Shear Rate 1000 – 1000 1/s
|
Average value: 396000 cP Grade Count:5 | |
| Linear Mold Shrinkage | 0.00100 – 0.00700 cm/cm | 0.00100 – 0.00700 in/in | Average value: 0.00327 cm/cm Grade Count:11 |
| Linear Mold Shrinkage, Transverse | 0.00500 – 0.0150 cm/cm | 0.00500 – 0.0150 in/in | Average value: 0.00940 cm/cm Grade Count:10 |
| Melt Flow | 2.00 – 15.0 g/10 min | 2.00 – 15.0 g/10 min | Average value: 8.40 g/10 min Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 100 – 105 | 100 – 105 | Average value: 102 Grade Count:5 |
| Tensile Strength, Ultimate | 110 – 191 MPa | 16000 – 27700 psi | Average value: 156 MPa Grade Count:11 |
| 50.0 – 205 MPa
@Temperature -50.0 – 250 °C
|
7250 – 29700 psi
@Temperature -58.0 – 482 °F
|
Average value: 124 MPa Grade Count:1 | |
| Tensile Strength, Yield | 158 – 188 MPa | 22900 – 27300 psi | Average value: 168 MPa Grade Count:4 |
| Elongation at Break | 1.80 – 3.20 % | 1.80 – 3.20 % | Average value: 2.53 % Grade Count:10 |
| Modulus of Elasticity | 6.20 – 16.7 GPa | 899 – 2420 ksi | Average value: 11.1 GPa Grade Count:11 |
| Flexural Yield Strength | 160 – 283 MPa | 23200 – 41000 psi | Average value: 235 MPa Grade Count:11 |
| 54.0 – 54.0 MPa
@Temperature 250 – 250 °C
|
7830 – 7830 psi
@Temperature 482 – 482 °F
|
Average value: 54.0 MPa Grade Count:1 | |
| Flexural Modulus | 5.50 – 15.4 GPa | 798 – 2230 ksi | Average value: 10.0 GPa Grade Count:11 |
| Compressive Yield Strength | 139 – 182 MPa | 20200 – 26400 psi | Average value: 162 MPa Grade Count:5 |
| Shear Strength | 80.8 – 89.0 MPa | 11700 – 12900 psi | Average value: 84.3 MPa Grade Count:5 |
| Izod Impact, Notched | 0.500 – 1.20 J/cm | 0.937 – 2.25 ft-lb/in | Average value: 0.858 J/cm Grade Count:10 |
| Izod Impact, Unnotched | 4.30 – 10.0 J/cm | 8.06 – 18.7 ft-lb/in | Average value: 7.86 J/cm Grade Count:10 |
| Izod Impact, Notched (ISO) | 8.50 – 14.0 kJ/m² | 4.04 – 6.66 ft-lb/in² | Average value: 11.9 kJ/m² Grade Count:4 |
| Izod Impact, Unnotched (ISO) | 41.0 – 70.0 kJ/m² | 19.5 – 33.3 ft-lb/in² | Average value: 61.0 kJ/m² Grade Count:4 |
| K (wear) Factor | 10100 x 10-8 mm³/N-M | 5000 x 10-10 in³-min/ft-lb-hr | Average value: 10100 x 10<sup>-8</sup> mm³/N-M Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.0 – 19.0 µm/m-°C | 8.33 – 10.6 µin/in-°F | Average value: 17.0 µm/m-°C Grade Count:4 |
| Specific Heat Capacity | 1.26 – 1.70 J/g-°C
@Temperature 50.0 – 200 °C
|
0.301 – 0.406 BTU/lb-°F
@Temperature 122 – 392 °F
|
Average value: 1.47 J/g-°C Grade Count:5 |
| Thermal Conductivity | 0.280 – 0.310 W/m-K | 1.94 – 2.15 BTU-in/hr-ft²-°F | Average value: 0.294 W/m-K Grade Count:5 |
| Melting Point | 340 – 372 °C | 644 – 702 °F | Average value: 347 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 – 360 °C | 408 – 680 °F | Average value: 268 °C Grade Count:10 |
| Glass Transition Temp, Tg | 150 – 158 °C | 302 – 316 °F | Average value: 156 °C Grade Count:6 |
| Flammability, UL94 | V-1 – V-0 | V-1 – V-0 | Grade Count:9 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 – 2.10e+17 ohm-cm | 1.00e+16 – 2.10e+17 ohm-cm | Average value: 9.11e+16 ohm-cm Grade Count:9 |
| Surface Resistance | 1.00e+16 – 1.90e+17 ohm | 1.00e+16 – 1.90e+17 ohm | Average value: 1.54e+17 ohm Grade Count:5 |
| Dielectric Constant | 3.48 – 3.74 | 3.48 – 3.74 | Average value: 3.62 Grade Count:5 |
| Dielectric Strength | 14.0 – 19.0 kV/mm | 356 – 483 kV/in | Average value: 15.7 kV/mm Grade Count:10 |
| Dissipation Factor | 0.000 – 0.00600 | 0.000 – 0.00600 | Average value: 0.00243 Grade Count:5 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 360 – 425 °C | 680 – 797 °F | Average value: 387 °C Grade Count:6 |
| Melt Temperature | 360 – 404 °C | 680 – 759 °F | Average value: 374 °C Grade Count:6 |
| Mold Temperature | 149 – 220 °C | 300 – 428 °F | Average value: 181 °C Grade Count:7 |
| Drying Temperature | 149 – 175 °C | 300 – 347 °F | Average value: 151 °C Grade Count:7 |