Overview of materials for Polyethersulfone, Carbon Fiber Reinforced
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polyethersulfone, Carbon Fiber Reinforced”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 – 1.57 g/cc | 0.0491 – 0.0567 lb/in³ | Average value: 1.45 g/cc Grade Count:30 |
| Filler Content | 10.0 – 40.0 % | 10.0 – 40.0 % | Average value: 19.6 % Grade Count:14 |
| Water Absorption | 0.100 – 1.50 % | 0.100 – 1.50 % | Average value: 0.386 % Grade Count:15 |
| Additive Loading | 10.0 – 40.0 % | 10.0 – 40.0 % | Average value: 23.3 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000500 – 0.00400 cm/cm | 0.000500 – 0.00400 in/in | Average value: 0.00188 cm/cm Grade Count:28 |
| Melt Flow | 12.1 – 15.3 g/10 min | 12.1 – 15.3 g/10 min | Average value: 14.1 g/10 min Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 90.0 – 325 MPa | 13100 – 47100 psi | Average value: 146 MPa Grade Count:29 |
| Elongation at Break | 1.00 – 12.0 % | 1.00 – 12.0 % | Average value: 2.35 % Grade Count:24 |
| Elongation at Yield | 1.30 – 2.80 % | 1.30 – 2.80 % | Average value: 2.10 % Grade Count:5 |
| Modulus of Elasticity | 2.40 – 36.6 GPa | 348 – 5300 ksi | Average value: 14.3 GPa Grade Count:30 |
| Flexural Yield Strength | 125 – 303 MPa | 18100 – 44000 psi | Average value: 219 MPa Grade Count:28 |
| Flexural Modulus | 2.60 – 24.1 GPa | 377 – 3500 ksi | Average value: 12.5 GPa Grade Count:29 |
| Izod Impact, Notched | 0.534 – 1.60 J/cm | 1.00 – 3.00 ft-lb/in | Average value: 0.653 J/cm Grade Count:25 |
| Izod Impact, Unnotched | 3.74 – 6.94 J/cm | 7.00 – 13.0 ft-lb/in | Average value: 5.15 J/cm Grade Count:24 |
| Charpy Impact Unnotched | 1.90 – 2.00 J/cm² | 9.04 – 9.52 ft-lb/in² | Average value: 1.97 J/cm² Grade Count:3 |
| Charpy Impact, Notched | 0.450 – 0.600 J/cm² | 2.14 – 2.86 ft-lb/in² | Average value: 0.550 J/cm² Grade Count:3 |
| 0.300 – 0.300 J/cm²
@Temperature -30.0 – -30.0 °C
|
1.43 – 1.43 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 0.300 J/cm² Grade Count:1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.0 – 13.0 µm/m-°C
@Temperature 180 – 180 °C
|
7.22 – 7.22 µin/in-°F
@Temperature 356 – 356 °F
|
Average value: 27.9 µm/m-°C Grade Count:1 |
| 26.0 – 34.0 µm/m-°C
@Temperature 75.0 – 175 °C
|
14.4 – 18.9 µin/in-°F
@Temperature 167 – 347 °F
|
Average value: 27.9 µm/m-°C Grade Count:1 | |
| 26.0 – 34.0 µm/m-°C
@Thickness 2.00 – 4.00 mm
|
14.4 – 18.9 µin/in-°F
@Thickness 0.0787 – 0.157 in
|
Average value: 27.9 µm/m-°C Grade Count:1 | |
| CTE, linear, Transverse to Flow | 19.5 – 25.0 µm/m-°C
@Temperature 75.0 – 175 °C
|
10.8 – 13.9 µin/in-°F
@Temperature 167 – 347 °F
|
Average value: 22.3 µm/m-°C Grade Count:1 |
| 19.5 – 25.0 µm/m-°C
@Thickness 2.00 – 4.00 mm
|
10.8 – 13.9 µin/in-°F
@Thickness 0.0787 – 0.157 in
|
Average value: 22.3 µm/m-°C Grade Count:1 | |
| Maximum Service Temperature, Air | 180 – 200 °C | 356 – 392 °F | Average value: 190 °C Grade Count:4 |
| Deflection Temperature at 0.46 MPa (66 psi) | 207 – 210 °C | 405 – 410 °F | Average value: 208 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 – 410 °C | 295 – 770 °F | Average value: 216 °C Grade Count:27 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:21 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 100 – 9.90e+9 ohm-cm | 100 – 9.90e+9 ohm-cm | Average value: 6.61e+8 ohm-cm Grade Count:19 |
| Surface Resistance | 4000 – 1.00e+12 ohm | 4000 – 1.00e+12 ohm | Average value: 1.17e+11 ohm Grade Count:9 |
| Insulation Resistance | 100000 – 1.00e+6 ohm | 100000 – 1.00e+6 ohm | Average value: 775000 ohm Grade Count:4 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:5 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 – 366 °C | 176 – 690 °F | Average value: 322 °C Grade Count:9 |
| Nozzle Temperature | 340 – 360 °C | 644 – 680 °F | Average value: 350 °C Grade Count:4 |
| Melt Temperature | 343 – 390 °C | 650 – 734 °F | Average value: 362 °C Grade Count:24 |
| Mold Temperature | 120 – 200 °C | 248 – 392 °F | Average value: 157 °C Grade Count:28 |
| Drying Temperature | 140 – 150 °C | 284 – 302 °F | Average value: 149 °C Grade Count:24 |
| Moisture Content | 0.0400 % | 0.0400 % | Average value: 0.0400 % Grade Count:19 |
| Dew Point | -31.7 °C | -25.0 °F | Average value: -31.7 °C Grade Count:19 |
| Injection Pressure | 68.9 – 103 MPa | 10000 – 15000 psi | Average value: 86.2 MPa Grade Count:23 |