Overview of materials for Polyethersulfone (PES), 10% Glass Fiber Filled
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polyethersulfone (PES), 10% Glass Fiber Filled”. Specific grades with glass content between 5% and 14% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 – 1.70 g/cc | 0.0502 – 0.0614 lb/in³ | Average value: 1.50 g/cc Grade Count:19 |
| Filler Content | 5.00 – 10.0 % | 5.00 – 10.0 % | Average value: 8.75 % Grade Count:8 |
| Water Absorption | 0.100 – 0.400 % | 0.100 – 0.400 % | Average value: 0.225 % Grade Count:15 |
| Linear Mold Shrinkage | 0.00100 – 0.00800 cm/cm | 0.00100 – 0.00800 in/in | Average value: 0.00467 cm/cm Grade Count:19 |
| Melt Flow | 15.0 – 23.2 g/10 min | 15.0 – 23.2 g/10 min | Average value: 17.7 g/10 min Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 – 123 | 121 – 123 | Average value: 122 Grade Count:6 |
| Tensile Strength, Ultimate | 66.9 – 145 MPa | 9700 – 21000 psi | Average value: 109 MPa Grade Count:17 |
| 70.0 – 95.0 MPa
@Temperature 60.0 – 150 °C
|
10200 – 13800 psi
@Temperature 140 – 302 °F
|
Average value: 82.5 MPa Grade Count:1 | |
| Elongation at Break | 2.00 – 8.00 % | 2.00 – 8.00 % | Average value: 4.36 % Grade Count:11 |
| 3.70 – 20.0 %
@Temperature 60.0 – 150 °C
|
3.70 – 20.0 %
@Temperature 140 – 302 °F
|
Average value: 8.05 % Grade Count:1 | |
| Elongation at Yield | 1.60 – 4.80 % | 1.60 – 4.80 % | Average value: 2.86 % Grade Count:8 |
| 3.20 – 3.20 %
@Temperature 150 – 150 °C
|
3.20 – 3.20 %
@Temperature 302 – 302 °F
|
Average value: 3.20 % Grade Count:1 | |
| Modulus of Elasticity | 3.45 – 12.0 GPa | 500 – 1740 ksi | Average value: 6.11 GPa Grade Count:18 |
| 4.10 – 4.50 GPa
@Temperature 60.0 – 150 °C
|
595 – 653 ksi
@Temperature 140 – 302 °F
|
Average value: 4.33 GPa Grade Count:1 | |
| Flexural Yield Strength | 121 – 210 MPa | 17500 – 30500 psi | Average value: 161 MPa Grade Count:18 |
| Flexural Modulus | 3.45 – 10.0 GPa | 500 – 1450 ksi | Average value: 5.27 GPa Grade Count:18 |
| Compressive Yield Strength | 110 MPa | 16000 psi | Average value: 110 MPa Grade Count:3 |
| Izod Impact, Notched | 0.374 – 0.747 J/cm | 0.700 – 1.40 ft-lb/in | Average value: 0.587 J/cm Grade Count:10 |
| Izod Impact, Unnotched | 3.74 – 11.2 J/cm | 7.00 – 21.0 ft-lb/in | Average value: 5.94 J/cm Grade Count:8 |
| Charpy Impact Unnotched | 3.00 – 5.50 J/cm² | 14.3 – 26.2 ft-lb/in² | Average value: 4.40 J/cm² Grade Count:8 |
| Charpy Impact, Notched | 0.350 – 1.00 J/cm² | 1.67 – 4.76 ft-lb/in² | Average value: 0.836 J/cm² Grade Count:7 |
| Coefficient of Friction | 0.200 – 0.230 | 0.200 – 0.230 | Average value: 0.213 Grade Count:3 |
| Coefficient of Friction, Static | 0.150 – 0.230 | 0.150 – 0.230 | Average value: 0.193 Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 31.0 – 50.4 µm/m-°C | 17.2 – 28.0 µin/in-°F | Average value: 37.4 µm/m-°C Grade Count:9 |
| Thermal Conductivity | 0.288 – 0.380 W/m-K | 2.00 – 2.64 BTU-in/hr-ft²-°F | Average value: 0.321 W/m-K Grade Count:8 |
| Maximum Service Temperature, Air | 180 – 200 °C | 356 – 392 °F | Average value: 189 °C Grade Count:9 |
| Deflection Temperature at 0.46 MPa (66 psi) | 207 – 220 °C | 405 – 428 °F | Average value: 210 °C Grade Count:5 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 – 215 °C | 400 – 419 °F | Average value: 208 °C Grade Count:17 |
| Vicat Softening Point | 215 – 220 °C | 419 – 428 °F | Average value: 219 °C Grade Count:8 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:15 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+12 – 1.00e+16 ohm-cm | 1.00e+12 – 1.00e+16 ohm-cm | Average value: 6.38e+15 ohm-cm Grade Count:8 |
| Insulation Resistance | 1.00e+12 ohm | 1.00e+12 ohm | Average value: 1.00e+12 ohm Grade Count:8 |
| Dielectric Constant | 3.70 | 3.70 | Average value: 3.70 Grade Count:4 |
| Dielectric Strength | 15.0 – 21.7 kV/mm | 380 – 550 kV/in | Average value: 16.1 kV/mm Grade Count:6 |
| Dissipation Factor | 0.00700 | 0.00700 | Average value: 0.00700 Grade Count:4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 343 – 366 °C | 650 – 690 °F | Average value: 351 °C Grade Count:11 |
| Nozzle Temperature | 340 – 360 °C | 644 – 680 °F | Average value: 350 °C Grade Count:8 |
| Melt Temperature | 343 – 380 °C | 650 – 716 °F | Average value: 364 °C Grade Count:15 |
| Mold Temperature | 120 – 200 °C | 248 – 392 °F | Average value: 158 °C Grade Count:17 |
| Drying Temperature | 149 – 180 °C | 300 – 356 °F | Average value: 151 °C Grade Count:14 |
| Moisture Content | 0.0400 % | 0.0400 % | Average value: 0.0400 % Grade Count:5 |
| Dew Point | -31.7 °C | -25.0 °F | Average value: -31.7 °C Grade Count:5 |
| Injection Pressure | 68.9 – 103 MPa | 10000 – 15000 psi | Average value: 86.2 MPa Grade Count:8 |