Overview of materials for Polyphthalamide (PPA), Glass Fiber 40%
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polyphthalamide, Glass Fiber 40%”. Specific grades with glass content between 35% and 44% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 – 1.81 g/cc | 0.0499 – 0.0654 lb/in³ | Average value: 1.50 g/cc Grade Count:53 |
| 1.10 – 1.10 g/cc
@Temperature 325 – 325 °C
|
0.0397 – 0.0397 lb/in³
@Temperature 617 – 617 °F
|
Average value: 1.10 g/cc Grade Count:1 | |
| Filler Content | 35.0 – 40.0 % | 35.0 – 40.0 % | Average value: 38.9 % Grade Count:28 |
| Water Absorption | 0.0200 – 5.00 % | 0.0200 – 5.00 % | Average value: 0.826 % Grade Count:14 |
| 1.10 – 1.15 %
@Temperature 70.0 – 70.0 °C
|
1.10 – 1.15 %
@Temperature 158 – 158 °F
|
Average value: 1.12 % Grade Count:6 | |
| Linear Mold Shrinkage | 0.00100 – 0.0100 cm/cm | 0.00100 – 0.0100 in/in | Average value: 0.00374 cm/cm Grade Count:45 |
| Linear Mold Shrinkage, Transverse | 0.00450 – 0.105 cm/cm | 0.00450 – 0.105 in/in | Average value: 0.00982 cm/cm Grade Count:19 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 124 – 125 | 124 – 125 | Average value: 125 Grade Count:8 |
| Ball Indentation Hardness | 310 – 330 MPa | 45000 – 47900 psi | Average value: 322 MPa Grade Count:5 |
| Tensile Strength, Ultimate | 6.13 – 260 MPa | 889 – 37700 psi | Average value: 180 MPa Grade Count:54 |
| 65.0 – 230 MPa
@Temperature -40.0 – 200 °C
|
9430 – 33400 psi
@Temperature -40.0 – 392 °F
|
Average value: 98.0 MPa Grade Count:4 | |
| 120 – 130 MPa
@Temperature 130 – 180 °C
|
17400 – 18900 psi
@Temperature 266 – 356 °F
|
Average value: 98.0 MPa Grade Count:5 | |
| 120 – 130 MPa
@Time 1.80e+7 – 7.20e+7 sec
|
17400 – 18900 psi
@Time 5000 – 20000 hour
|
Average value: 98.0 MPa Grade Count:5 | |
| 3.94 – 237.87 MPa
@Strain 0.0400 – 5.10 %
|
571 – 34500 psi
@Strain 0.0400 – 5.10 %
|
Average value: 98.0 MPa Grade Count:2 | |
| 3.94 – 237.87 MPa
@Temperature -20.0 – 180 °C
|
571 – 34500 psi
@Temperature -4.00 – 356 °F
|
Average value: 98.0 MPa Grade Count:2 | |
| Elongation at Break | 1.00 – 4.50 % | 1.00 – 4.50 % | Average value: 2.34 % Grade Count:55 |
| 2.10 – 8.60 %
@Temperature -40.0 – 200 °C
|
2.10 – 8.60 %
@Temperature -40.0 – 392 °F
|
Average value: 4.42 % Grade Count:4 | |
| Modulus of Elasticity | 10.0 – 17.2 GPa | 1450 – 2500 ksi | Average value: 12.8 GPa Grade Count:52 |
| 2.333 – 13.0 GPa
@Temperature -40.0 – 230 °C
|
338.4 – 1890 ksi
@Temperature -40.0 – 446 °F
|
Average value: 7.20 GPa Grade Count:8 | |
| Flexural Yield Strength | 231 – 360 MPa | 33500 – 52200 psi | Average value: 299 MPa Grade Count:33 |
| 261 – 352 MPa
@Temperature -40.0 – 60.0 °C
|
37900 – 51100 psi
@Temperature -40.0 – 140 °F
|
Average value: 154 MPa Grade Count:1 | |
| 96.0 – 181 MPa
@Temperature 100 – 200 °C
|
13900 – 26300 psi
@Temperature 212 – 392 °F
|
Average value: 154 MPa Grade Count:2 | |
| 96.0 – 181 MPa
@Strain 3.50 – 5.00 %
|
13900 – 26300 psi
@Strain 3.50 – 5.00 %
|
Average value: 154 MPa Grade Count:2 | |
| Flexural Modulus | 8.30 – 15.9 GPa | 1200 – 2300 ksi | Average value: 12.2 GPa Grade Count:38 |
| 3.46 – 10.62 GPa
@Temperature -40.0 – 200 °C
|
502 – 1540 ksi
@Temperature -40.0 – 392 °F
|
Average value: 5.77 GPa Grade Count:2 | |
| Compressive Yield Strength | 71.0 – 355 MPa
@Temperature -40.0 – 200 °C
|
10300 – 51500 psi
@Temperature -40.0 – 392 °F
|
Average value: 171 MPa Grade Count:1 |
| Poissons Ratio | 0.380 – 0.390 | 0.380 – 0.390 | Average value: 0.387 Grade Count:4 |
| Shear Modulus | >= 0.0768 GPa
@Temperature -50.0 – 290 °C
|
>= 11.1 ksi
@Temperature -58.0 – 554 °F
|
Average value: 1.60 GPa Grade Count:1 |
| Shear Strength | 73.8 – 91.7 MPa | 10700 – 13300 psi | Average value: 83.1 MPa Grade Count:3 |
| Secant Modulus | 1.70799 – 14.8867 GPa
@Temperature 0.000 – 200 °C
|
247.727 – 2159.17 ksi
@Temperature 32.0 – 392 °F
|
Average value: 10.1 GPa Grade Count:1 |
| 1.70799 – 14.8867 GPa
@Strain 0.0500 – 4.13 %
|
247.727 – 2159.17 ksi
@Strain 0.0500 – 4.13 %
|
Average value: 10.1 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.650 – 2.94 J/cm | 1.22 – 5.50 ft-lb/in | Average value: 1.21 J/cm Grade Count:19 |
| 0.910 – 0.910 J/cm
@Temperature -40.0 – -40.0 °C
|
1.70 – 1.70 ft-lb/in
@Temperature -40.0 – -40.0 °F
|
Average value: 0.910 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 5.87 – 11.2 J/cm | 11.0 – 21.0 ft-lb/in | Average value: 7.62 J/cm Grade Count:14 |
| Izod Impact, Notched (ISO) | 8.50 – 12.0 kJ/m² | 4.04 – 5.71 ft-lb/in² | Average value: 10.2 kJ/m² Grade Count:8 |
| 8.00 – 10.0 kJ/m²
@Temperature -30.0 – -30.0 °C
|
3.81 – 4.76 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 9.33 kJ/m² Grade Count:2 | |
| Izod Impact, Unnotched (ISO) | 40.0 – 65.0 kJ/m² | 19.0 – 30.9 ft-lb/in² | Average value: 56.0 kJ/m² Grade Count:5 |
| 55.0 – 67.0 kJ/m²
@Temperature -30.0 – -30.0 °C
|
26.2 – 31.9 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 61.0 kJ/m² Grade Count:2 | |
| Charpy Impact Unnotched | 3.80 – 9.00 J/cm² | 18.1 – 42.8 ft-lb/in² | Average value: 6.26 J/cm² Grade Count:30 |
| 3.50 – 7.50 J/cm²
@Temperature -40.0 – -30.0 °C
|
16.7 – 35.7 ft-lb/in²
@Temperature -40.0 – -22.0 °F
|
Average value: 5.25 J/cm² Grade Count:10 | |
| Charpy Impact, Notched | 0.800 – 1.40 J/cm² | 3.81 – 6.66 ft-lb/in² | Average value: 1.01 J/cm² Grade Count:30 |
| 0.600 – 1.10 J/cm²
@Temperature -40.0 – -30.0 °C
|
2.86 – 5.24 ft-lb/in²
@Temperature -40.0 – -22.0 °F
|
Average value: 0.921 J/cm² Grade Count:11 | |
| Tensile Creep Modulus, 1 hour | 10000 – 11000 MPa | 1.45e+6 – 1.60e+6 psi | Average value: 10500 MPa Grade Count:4 |
| Tensile Creep Modulus, 1000 hours | 8500 – 10000 MPa | 1.23e+6 – 1.45e+6 psi | Average value: 9130 MPa Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | Average value: 1.00e+15 ohm-cm Grade Count:18 |
| Surface Resistance | 1.00e+13 – 1.00e+15 ohm | 1.00e+13 – 1.00e+15 ohm | Average value: 3.85e+14 ohm Grade Count:5 |
| Dielectric Constant | 3.80 – 5.80 | 3.80 – 5.80 | Average value: 4.30 Grade Count:8 |
| 4.20 – 136
@Temperature 60.0 – 200 °C
|
4.20 – 136
@Temperature 140 – 392 °F
|
Average value: 30.5 Grade Count:1 | |
| 4.20 – 136
@Frequency 1000 – 1.00e+6 Hz
|
4.20 – 136
@Frequency 1000 – 1.00e+6 Hz
|
Average value: 30.5 Grade Count:1 | |
| Dielectric Strength | 19.7 – 43.0 kV/mm | 500 – 1090 kV/in | Average value: 33.0 kV/mm Grade Count:13 |