Overview of materials for Polypropylene, Carbon Fiber Filled
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene, Carbon Fiber 10%”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.872 – 1.23 g/cc | 0.0315 – 0.0444 lb/in³ | Average value: 1.02 g/cc Grade Count:19 |
| Filler Content | 1.00 – 50.0 % | 1.00 – 50.0 % | Average value: 19.7 % Grade Count:14 |
| Water Absorption | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:7 |
| Linear Mold Shrinkage | 0.000500 – 0.0100 cm/cm | 0.000500 – 0.0100 in/in | Average value: 0.00311 cm/cm Grade Count:14 |
| Melt Flow | 1.10 – 9.80 g/10 min | 1.10 – 9.80 g/10 min | Average value: 4.93 g/10 min Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 19.3 – 117 MPa | 2800 – 17000 psi | Average value: 45.5 MPa Grade Count:20 |
| Elongation at Break | 0.400 – 436 % | 0.400 – 436 % | Average value: 34.4 % Grade Count:22 |
| Modulus of Elasticity | 1.03 – 27.6 GPa | 150 – 4000 ksi | Average value: 9.05 GPa Grade Count:20 |
| Flexural Yield Strength | 31.0 – 186 MPa | 4500 – 27000 psi | Average value: 75.4 MPa Grade Count:18 |
| Flexural Modulus | 2.76 – 19.3 GPa | 400 – 2800 ksi | Average value: 8.51 GPa Grade Count:18 |
| Izod Impact, Notched | 0.427 – 3.20 J/cm | 0.800 – 6.00 ft-lb/in | Average value: 1.14 J/cm Grade Count:16 |
| Izod Impact, Unnotched | 1.07 – 11.2 J/cm | 2.00 – 21.0 ft-lb/in | Average value: 3.74 J/cm Grade Count:17 |
| Charpy Impact, Notched | 0.240 – 0.320 J/cm² | 1.14 – 1.52 ft-lb/in² | Average value: 0.290 J/cm² Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | Average value: 165 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 – 166 °C | 270 – 330 °F | Average value: 143 °C Grade Count:5 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 – 149 °C | 220 – 300 °F | Average value: 130 °C Grade Count:11 |
| Flammability, UL94 | HB | HB | Grade Count:7 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00 – 3.10e+9 ohm-cm | 1.00 – 3.10e+9 ohm-cm | Average value: 2.40e+8 ohm-cm Grade Count:16 |
| Surface Resistance | 100 – 1.10e+11 ohm | 100 – 1.10e+11 ohm | Average value: 1.56e+10 ohm Grade Count:12 |
| Static Decay | 0.100 – 2.00 sec | 0.100 – 2.00 sec | Average value: 1.51 sec Grade Count:7 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 188 – 227 °C | 370 – 440 °F | Average value: 209 °C Grade Count:8 |
| Nozzle Temperature | 204 – 216 °C | 400 – 420 °F | Average value: 210 °C Grade Count:3 |
| Melt Temperature | 191 – 250 °C | 375 – 482 °F | Average value: 214 °C Grade Count:9 |
| Mold Temperature | 30.0 – 79.4 °C | 86.0 – 175 °F | Average value: 53.5 °C Grade Count:17 |
| Injection Velocity | 50.8 – 76.2 mm/sec | 2.00 – 3.00 in/sec | Average value: 63.5 mm/sec Grade Count:3 |
| Drying Temperature | 70.0 – 79.4 °C | 158 – 175 °F | Average value: 77.9 °C Grade Count:6 |
| Injection Pressure | 68.9 – 103 MPa | 10000 – 15000 psi | Average value: 86.2 MPa Grade Count:13 |
| Cushion | 0.635 cm | 0.250 in | Average value: 0.635 cm Grade Count:3 |