Overview of materials for Polypropylene Glass Bead Filled
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene Glass Bead Filled”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.770 – 1.40 g/cc | 0.0278 – 0.0506 lb/in³ | Average value: 1.08 g/cc Grade Count:30 |
| Filler Content | 10.0 – 40.0 % | 10.0 – 40.0 % | Average value: 25.0 % Grade Count:6 |
| Water Absorption | 0.0200 – 0.0400 % | 0.0200 – 0.0400 % | Average value: 0.0258 % Grade Count:12 |
| Linear Mold Shrinkage | 0.00800 – 0.0226 cm/cm | 0.00800 – 0.0226 in/in | Average value: 0.0143 cm/cm Grade Count:26 |
| Linear Mold Shrinkage, Transverse | 0.00900 – 0.0210 cm/cm | 0.00900 – 0.0210 in/in | Average value: 0.0153 cm/cm Grade Count:8 |
| Melt Flow | 3.00 – 25.0 g/10 min | 3.00 – 25.0 g/10 min | Average value: 9.65 g/10 min Grade Count:10 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 89.0 – 100 | 89.0 – 100 | Average value: 96.2 Grade Count:10 |
| Tensile Strength, Ultimate | 6.21 – 37.0 MPa | 900 – 5370 psi | Average value: 23.9 MPa Grade Count:23 |
| Tensile Strength, Yield | 17.6 – 26.2 MPa | 2550 – 3800 psi | Average value: 21.3 MPa Grade Count:9 |
| Elongation at Break | 2.00 – 100 % | 2.00 – 100 % | Average value: 21.0 % Grade Count:22 |
| Elongation at Yield | 4.80 – 100 % | 4.80 – 100 % | Average value: 19.4 % Grade Count:8 |
| Modulus of Elasticity | 1.32 – 3.25 GPa | 191 – 471 ksi | Average value: 2.08 GPa Grade Count:23 |
| Flexural Yield Strength | 10.3 – 55.0 MPa | 1500 – 7980 psi | Average value: 35.6 MPa Grade Count:26 |
| Flexural Modulus | 1.03 – 3.10 GPa | 149 – 450 ksi | Average value: 1.89 GPa Grade Count:27 |
| Compressive Yield Strength | 29.0 – 34.5 MPa | 4200 – 5000 psi | Average value: 32.1 MPa Grade Count:4 |
| Izod Impact, Notched | 0.160 – 1.60 J/cm | 0.300 – 3.00 ft-lb/in | Average value: 0.404 J/cm Grade Count:21 |
| Izod Impact, Unnotched | 1.87 – 10.7 J/cm | 3.50 – 20.0 ft-lb/in | Average value: 4.43 J/cm Grade Count:13 |
| Izod Impact, Notched (ISO) | 2.70 – 6.00 kJ/m² | 1.28 – 2.86 ft-lb/in² | Average value: 3.67 kJ/m² Grade Count:4 |
| 4.00 – 4.00 kJ/m²
@Temperature -30.0 – -30.0 °C
|
1.90 – 1.90 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 4.00 kJ/m² Grade Count:1 | |
| Charpy Impact Unnotched | 1.50 – 4.50 J/cm² | 7.14 – 21.4 ft-lb/in² | Average value: 3.37 J/cm² Grade Count:7 |
| 1.80 – 3.40 J/cm²
@Temperature -20.0 – -20.0 °C
|
8.57 – 16.2 ft-lb/in²
@Temperature -4.00 – -4.00 °F
|
Average value: 2.44 J/cm² Grade Count:5 | |
| Charpy Impact, Notched | 0.300 – 0.600 J/cm² | 1.43 – 2.86 ft-lb/in² | Average value: 0.467 J/cm² Grade Count:6 |
| 0.200 – 0.500 J/cm²
@Temperature -20.0 – -20.0 °C
|
0.952 – 2.38 ft-lb/in²
@Temperature -4.00 – -4.00 °F
|
Average value: 0.340 J/cm² Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 37.8 – 104 µm/m-°C | 21.0 – 57.8 µin/in-°F | Average value: 62.9 µm/m-°C Grade Count:10 |
| Melting Point | 150 – 170 °C | 302 – 338 °F | Average value: 164 °C Grade Count:14 |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 – 125 °C | 190 – 257 °F | Average value: 114 °C Grade Count:14 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 – 160 °C | 133 – 320 °F | Average value: 77.4 °C Grade Count:26 |
| Vicat Softening Point | 94.0 – 156 °C | 201 – 313 °F | Average value: 114 °C Grade Count:8 |
| Flammability, UL94 | HB | HB | Grade Count:15 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+12 – 1.00e+17 ohm-cm | 1.00e+12 – 1.00e+17 ohm-cm | Average value: 1.47e+16 ohm-cm Grade Count:13 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Average value: 19.7 kV/mm Grade Count:6 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 193 – 240 °C | 380 – 464 °F | Average value: 211 °C Grade Count:7 |
| Melt Temperature | 191 – 250 °C | 375 – 482 °F | Average value: 221 °C Grade Count:15 |
| Mold Temperature | 20.0 – 80.0 °C | 68.0 – 176 °F | Average value: 50.1 °C Grade Count:22 |
| Drying Temperature | 70.0 – 100 °C | 158 – 212 °F | Average value: 79.9 °C Grade Count:11 |
| Injection Pressure | 60.0 – 120 MPa | 8700 – 17400 psi | Average value: 87.9 MPa Grade Count:18 |