Overview of materials for Polypropylene, Stainless Fiber, EMI
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene, Stainless Fiber, EMI”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 – 1.30 g/cc | 0.0347 – 0.0470 lb/in³ | Average value: 1.05 g/cc Grade Count:13 |
| Filler Content | 5.00 – 15.0 % | 5.00 – 15.0 % | Average value: 10.0 % Grade Count:4 |
| Water Absorption | 0.0100 – 0.0200 % | 0.0100 – 0.0200 % | Average value: 0.0125 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00300 – 0.0250 cm/cm | 0.00300 – 0.0250 in/in | Average value: 0.00889 cm/cm Grade Count:11 |
| Linear Mold Shrinkage, Transverse | 0.0140 – 0.0250 cm/cm | 0.0140 – 0.0250 in/in | Average value: 0.0209 cm/cm Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 15.0 – 70.0 MPa | 2180 – 10200 psi | Average value: 33.4 MPa Grade Count:13 |
| Tensile Strength, Yield | 19.0 – 21.4 MPa | 2760 – 3100 psi | Average value: 20.5 MPa Grade Count:3 |
| Elongation at Break | 2.50 – 76.0 % | 2.50 – 76.0 % | Average value: 23.5 % Grade Count:13 |
| Elongation at Yield | 5.20 – 8.00 % | 5.20 – 8.00 % | Average value: 6.60 % Grade Count:4 |
| Modulus of Elasticity | 0.965 – 4.10 GPa | 140 – 595 ksi | Average value: 2.04 GPa Grade Count:12 |
| Flexural Yield Strength | 27.6 – 109 MPa | 4000 – 15800 psi | Average value: 48.5 MPa Grade Count:12 |
| Flexural Modulus | 1.10 – 6.20 GPa | 160 – 899 ksi | Average value: 2.50 GPa Grade Count:12 |
| Izod Impact, Notched | 0.600 – 2.67 J/cm | 1.12 – 5.00 ft-lb/in | Average value: 1.60 J/cm Grade Count:10 |
| Izod Impact, Unnotched | 3.20 – 5340 J/cm | 5.99 – 10000 ft-lb/in | Average value: 8.36 J/cm Grade Count:10 |
| Izod Impact, Notched (ISO) | 10.0 – 25.0 kJ/m² | 4.76 – 11.9 ft-lb/in² | Average value: 20.0 kJ/m² Grade Count:3 |
| K (wear) Factor | 10100 x 10-8 mm³/N-M | 5000 x 10-10 in³-min/ft-lb-hr | Average value: 10100 x 10<sup>-8</sup> mm³/N-M Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 54.0 – 140 µm/m-°C | 30.0 – 77.8 µin/in-°F | Average value: 103 µm/m-°C Grade Count:4 |
| CTE, linear, Transverse to Flow | 120 – 170 µm/m-°C | 66.7 – 94.4 µin/in-°F | Average value: 150 µm/m-°C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 – 138 °C | 203 – 280 °F | Average value: 124 °C Grade Count:7 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.8 – 138 °C | 127 – 280 °F | Average value: 86.8 °C Grade Count:9 |
| Flammability, UL94 | HB | HB | Grade Count:6 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0100 – 100 ohm-cm | 0.0100 – 100 ohm-cm | Average value: 22.6 ohm-cm Grade Count:9 |
| Surface Resistance | 10.0 – 1.00e+6 ohm | 10.0 – 1.00e+6 ohm | Average value: 169000 ohm Grade Count:9 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:6 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 188 – 227 °C | 370 – 440 °F | Average value: 204 °C Grade Count:3 |
| Melt Temperature | 180 – 246 °C | 356 – 475 °F | Average value: 219 °C Grade Count:7 |
| Mold Temperature | 20.0 – 65.6 °C | 68.0 – 150 °F | Average value: 43.0 °C Grade Count:10 |
| Drying Temperature | 79.4 – 90.0 °C | 175 – 194 °F | Average value: 81.4 °C Grade Count:7 |
| Moisture Content | 0.100 % | 0.100 % | Average value: 0.100 % Grade Count:3 |
| Injection Pressure | 68.9 – 103 MPa | 10000 – 15000 psi | Average value: 86.2 MPa Grade Count:6 |