Overview of materials for Polypropylene with 30% Mica Filler
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene with 30% Mica Filler”. Specific grades with primary filler content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 – 1.49 g/cc | 0.0390 – 0.0538 lb/in³ | Average value: 1.13 g/cc Grade Count:26 |
| Filler Content | 25.0 – 40.0 % | 25.0 – 40.0 % | Average value: 27.3 % Grade Count:11 |
| Water Absorption | 0.0200 – 0.0300 % | 0.0200 – 0.0300 % | Average value: 0.0267 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00400 – 0.0130 cm/cm | 0.00400 – 0.0130 in/in | Average value: 0.00840 cm/cm Grade Count:25 |
| Melt Flow | 4.00 – 20.0 g/10 min | 4.00 – 20.0 g/10 min | Average value: 11.1 g/10 min Grade Count:16 |
| Ash | 30.0 % | 30.0 % | Average value: 30.0 % Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 30.0 – 98.0 | 30.0 – 98.0 | Average value: 65.3 Grade Count:12 |
| Hardness, Shore D | 72.0 – 73.0 | 72.0 – 73.0 | Average value: 72.4 Grade Count:5 |
| Tensile Strength, Ultimate | 14.0 – 33.8 MPa | 2030 – 4900 psi | Average value: 26.2 MPa Grade Count:22 |
| Tensile Strength, Yield | 15.0 – 41.4 MPa | 2180 – 6000 psi | Average value: 29.8 MPa Grade Count:13 |
| Elongation at Break | 2.50 – 15.0 % | 2.50 – 15.0 % | Average value: 8.50 % Grade Count:19 |
| Elongation at Yield | 1.50 – 5.00 % | 1.50 – 5.00 % | Average value: 3.19 % Grade Count:13 |
| Modulus of Elasticity | 2.00 – 6.21 GPa | 290 – 900 ksi | Average value: 3.61 GPa Grade Count:14 |
| Flexural Yield Strength | 21.0 – 51.7 MPa | 3050 – 7500 psi | Average value: 42.2 MPa Grade Count:17 |
| Flexural Modulus | 2.10 – 5.52 GPa | 305 – 800 ksi | Average value: 3.31 GPa Grade Count:25 |
| Izod Impact, Notched | 0.214 – 1.49 J/cm | 0.400 – 2.80 ft-lb/in | Average value: 0.523 J/cm Grade Count:25 |
| Izod Impact, Unnotched | 1.07 – 6.41 J/cm | 2.00 – 12.0 ft-lb/in | Average value: 3.51 J/cm Grade Count:8 |
| Gardner Impact | 0.451 – 2.26 J | 0.333 – 1.67 ft-lb | Average value: 1.13 J Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.2 – 149 °C | 207 – 300 °F | Average value: 122 °C Grade Count:21 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 – 130 °C | 131 – 266 °F | Average value: 81.1 °C Grade Count:24 |
| Flammability, UL94 | HB – V-0 | HB – V-0 | Grade Count:8 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 216 – 232 °C | 420 – 450 °F | Average value: 222 °C Grade Count:5 |
| Melt Temperature | 191 – 243 °C | 375 – 470 °F | Average value: 218 °C Grade Count:10 |
| Mold Temperature | 26.7 – 65.6 °C | 80.0 – 150 °F | Average value: 43.4 °C Grade Count:10 |
| Drying Temperature | 65.6 – 90.0 °C | 150 – 194 °F | Average value: 77.2 °C Grade Count:10 |
| Moisture Content | 0.0500 % | 0.0500 % | Average value: 0.0500 % Grade Count:5 |
| Injection Pressure | 2.76 – 103 MPa | 400 – 15000 psi | Average value: 41.9 MPa Grade Count:9 |