Overview of materials for Polypropylene with 60% Glass Fiber Filler
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene with 60% Glass Fiber Filler”. Specific grades with glass content between 55% and 64% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 – 1.50 g/cc | 0.0415 – 0.0542 lb/in³ | Average value: 1.43 g/cc Grade Count:19 |
| Filler Content | 60.0 % | 60.0 % | Average value: 60.0 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00100 – 0.00600 cm/cm | 0.00100 – 0.00600 in/in | Average value: 0.00376 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 117 – 280 MPa | 17000 – 40600 psi | Average value: 151 MPa Grade Count:11 |
| 80.0 – 90.0 MPa
@Temperature 80.0 – 80.0 °C
|
11600 – 13100 psi
@Temperature 176 – 176 °F
|
Average value: 85.3 MPa Grade Count:4 | |
| Tensile Strength, Yield | 16.5 – 150 MPa | 2400 – 21800 psi | Average value: 111 MPa Grade Count:7 |
| Elongation at Break | 1.00 – 3.00 % | 1.00 – 3.00 % | Average value: 1.81 % Grade Count:17 |
| 2.00 – 2.10 %
@Temperature 80.0 – 80.0 °C
|
2.00 – 2.10 %
@Temperature 176 – 176 °F
|
Average value: 2.03 % Grade Count:4 | |
| Modulus of Elasticity | 6.30 – 25.1 GPa | 914 – 3640 ksi | Average value: 14.1 GPa Grade Count:16 |
| 9.10 – 9.50 GPa
@Temperature 80.0 – 80.0 °C
|
1320 – 1380 ksi
@Temperature 176 – 176 °F
|
Average value: 9.40 GPa Grade Count:4 | |
| Flexural Yield Strength | 28.3 – 420 MPa | 4100 – 60900 psi | Average value: 215 MPa Grade Count:18 |
| 134 – 140 MPa
@Temperature 80.0 – 80.0 °C
|
19400 – 20300 psi
@Temperature 176 – 176 °F
|
Average value: 137 MPa Grade Count:4 | |
| Flexural Modulus | 2.41 – 24.1 GPa | 350 – 3500 ksi | Average value: 13.0 GPa Grade Count:18 |
| 9.50 – 11.0 GPa
@Temperature 80.0 – 80.0 °C
|
1380 – 1600 ksi
@Temperature 176 – 176 °F
|
Average value: 10.2 GPa Grade Count:4 | |
| Izod Impact, Notched | 0.320 – 3.42 J/cm | 0.600 – 6.41 ft-lb/in | Average value: 2.36 J/cm Grade Count:7 |
| Charpy Impact Unnotched | 4.50 – 8.00 J/cm² | 21.4 – 38.1 ft-lb/in² | Average value: 6.56 J/cm² Grade Count:8 |
| 4.50 – 9.00 J/cm²
@Temperature -30.0 – -20.0 °C
|
21.4 – 42.8 ft-lb/in²
@Temperature -22.0 – -4.00 °F
|
Average value: 6.50 J/cm² Grade Count:7 | |
| Charpy Impact, Notched | 1.10 – 4.80 J/cm² | 5.24 – 22.8 ft-lb/in² | Average value: 2.98 J/cm² Grade Count:10 |
| 0.900 – 5.00 J/cm²
@Temperature -30.0 – -20.0 °C
|
4.28 – 23.8 ft-lb/in²
@Temperature -22.0 – -4.00 °F
|
Average value: 3.24 J/cm² Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 – 170 °C | 320 – 338 °F | Average value: 166 °C Grade Count:9 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 – 175 °C | 185 – 347 °F | Average value: 154 °C Grade Count:17 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 30.0 – 270 °C | 86.0 – 518 °F | Average value: 158 °C Grade Count:7 |
| Die Temperature | 240 – 250 °C | 464 – 482 °F | Average value: 245 °C Grade Count:7 |
| Melt Temperature | 199 – 270 °C | 390 – 518 °F | Average value: 239 °C Grade Count:10 |
| Mold Temperature | 37.8 – 90.0 °C | 100 – 194 °F | Average value: 72.2 °C Grade Count:3 |
| Drying Temperature | 80.0 – 100 °C | 176 – 212 °F | Average value: 91.7 °C Grade Count:9 |
| Moisture Content | 0.0200 – 0.200 % | 0.0200 – 0.200 % | Average value: 0.174 % Grade Count:7 |
| Injection Pressure | 60.0 – 140 MPa | 8700 – 20300 psi | Average value: 92.9 MPa Grade Count:9 |