Overview of materials for Polypropylene with Carbon Black Filler
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene with Carbon Black Filler”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.947 – 1.10 g/cc | 0.0342 – 0.0397 lb/in³ | Average value: 1.00 g/cc Grade Count:18 |
| Water Absorption | 0.0100 – 0.0300 % | 0.0100 – 0.0300 % | Average value: 0.0167 % Grade Count:3 |
| Thickness | 102 microns | 4.00 mil | Average value: 102 microns Grade Count:8 |
| Linear Mold Shrinkage | 0.0100 – 0.0200 cm/cm | 0.0100 – 0.0200 in/in | Average value: 0.0146 cm/cm Grade Count:13 |
| Melt Flow | 0.400 – 35.0 g/10 min | 0.400 – 35.0 g/10 min | Average value: 8.14 g/10 min Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 96.0 – 99.0 | 96.0 – 99.0 | Average value: 97.5 Grade Count:8 |
| Hardness, Shore D | 70.0 – 74.0 | 70.0 – 74.0 | Average value: 72.3 Grade Count:8 |
| Tensile Strength, Ultimate | 16.5 – 32.0 MPa | 2390 – 4640 psi | Average value: 23.4 MPa Grade Count:11 |
| Tensile Strength, Yield | 20.7 – 44.8 MPa | 3000 – 6500 psi | Average value: 26.8 MPa Grade Count:7 |
| Film Elongation at Break, MD | 4.00 – 500 % | 4.00 – 500 % | Average value: 252 % Grade Count:4 |
| Elongation at Break | 2.00 – 130 % | 2.00 – 130 % | Average value: 23.0 % Grade Count:13 |
| Elongation at Yield | 7.00 – 12.0 % | 7.00 – 12.0 % | Average value: 9.28 % Grade Count:5 |
| Modulus of Elasticity | 0.483 – 2.20 GPa | 70.1 – 319 ksi | Average value: 1.31 GPa Grade Count:3 |
| Flexural Yield Strength | 20.7 – 48.0 MPa | 3000 – 6960 psi | Average value: 30.0 MPa Grade Count:7 |
| Flexural Modulus | 0.965 – 3.10 GPa | 140 – 450 ksi | Average value: 1.67 GPa Grade Count:17 |
| Izod Impact, Notched | 0.502 – 8.33 J/cm | 0.940 – 15.6 ft-lb/in | Average value: 3.63 J/cm Grade Count:7 |
| Izod Impact, Unnotched | 1.00 J/cm – NB | 1.87 ft-lb/in – NB | Average value: 7.43 J/cm Grade Count:7 |
| Izod Impact, Notched (ISO) | 1.50 kJ/m² – NB | 0.714 ft-lb/in² – NB | Average value: 27.7 kJ/m² Grade Count:10 |
| 1.20 kJ/m² – NB
@Temperature -20.0 – -20.0 °C
|
0.571 ft-lb/in² – NB
@Temperature -4.00 – -4.00 °F
|
Average value: 5.84 kJ/m² Grade Count:7 | |
| 1.20 kJ/m² – NB
@Thickness 4.00 – 4.00 mm
|
0.571 ft-lb/in² – NB
@Thickness 0.157 – 0.157 in
|
Average value: 5.84 kJ/m² Grade Count:7 | |
| Izod Impact, Unnotched (ISO) | 16.0 kJ/m² – NB | 7.61 ft-lb/in² – NB | Average value: 48.7 kJ/m² Grade Count:10 |
| 9.00 kJ/m² – NB
@Temperature -20.0 – -20.0 °C
|
4.28 ft-lb/in² – NB
@Temperature -4.00 – -4.00 °F
|
Average value: 17.7 kJ/m² Grade Count:7 | |
| 9.00 kJ/m² – NB
@Thickness 4.00 – 4.00 mm
|
4.28 ft-lb/in² – NB
@Thickness 0.157 – 0.157 in
|
Average value: 17.7 kJ/m² Grade Count:7 | |
| Charpy Impact Unnotched | 1.40 – 1000 J/cm² | 6.66 – 4760 ft-lb/in² | Average value: 1.40 J/cm² Grade Count:8 |
| 0.500 – 999.9 J/cm²
@Temperature -20.0 – -20.0 °C
|
2.38 – 4759 ft-lb/in²
@Temperature -4.00 – -4.00 °F
|
Average value: 0.500 J/cm² Grade Count:7 | |
| 0.500 – 999.9 J/cm²
@Thickness 102 – 102 mm
|
2.38 – 4759 ft-lb/in²
@Thickness 4.00 – 4.00 in
|
Average value: 0.500 J/cm² Grade Count:7 | |
| Charpy Impact, Notched | 0.300 – 5.00 J/cm² | 1.43 – 23.8 ft-lb/in² | Average value: 2.44 J/cm² Grade Count:8 |
| 0.200 – 2.60 J/cm²
@Temperature -20.0 – -20.0 °C
|
0.952 – 12.4 ft-lb/in²
@Temperature -4.00 – -4.00 °F
|
Average value: 1.39 J/cm² Grade Count:7 | |
| 0.200 – 2.60 J/cm²
@Thickness 102 – 102 mm
|
0.952 – 12.4 ft-lb/in²
@Thickness 4.00 – 4.00 in
|
Average value: 1.39 J/cm² Grade Count:7 | |
| Film Tensile Strength at Break, MD | 25.0 – 33.0 MPa | 3630 – 4790 psi | Average value: 28.3 MPa Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 107 – 300 °C | 225 – 572 °F | Average value: 185 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 – 149 °C | 165 – 300 °F | Average value: 99.8 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 – 71.0 °C | 115 – 160 °F | Average value: 55.8 °C Grade Count:13 |
| Vicat Softening Point | 80.0 – 156 °C | 176 – 313 °F | Average value: 134 °C Grade Count:8 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 5.00 – 1.00e+9 ohm-cm | 5.00 – 1.00e+9 ohm-cm | Average value: 7.19e+7 ohm-cm Grade Count:15 |
| Surface Resistance | 10.0 – 1.00e+9 ohm | 10.0 – 1.00e+9 ohm | Average value: 6.72e+7 ohm Grade Count:17 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 270 °C | 392 – 518 °F | Average value: 229 °C Grade Count:11 |
| Mold Temperature | 32.2 – 80.0 °C | 90.0 – 176 °F | Average value: 58.9 °C Grade Count:7 |
| Roll Temperature | 60.0 – 100 °C | 140 – 212 °F | Average value: 80.7 °C Grade Count:5 |
| Drying Temperature | 60.0 – 82.2 °C | 140 – 180 °F | Average value: 72.4 °C Grade Count:10 |
| Injection Pressure | 60.0 – 80.0 MPa | 8700 – 11600 psi | Average value: 70.0 MPa Grade Count:4 |