Overview of materials for Polystyrene + Polyphenylene Ether, Glass + Mineral Filler
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polystyrene + Polyphenylene Ether, Glass + Mineral Filler”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 – 1.43 g/cc | 0.0434 – 0.0517 lb/in³ | Average value: 1.28 g/cc Grade Count:10 |
| Water Absorption | 0.0600 – 0.100 % | 0.0600 – 0.100 % | Average value: 0.0733 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000800 – 0.00800 cm/cm | 0.000800 – 0.00800 in/in | Average value: 0.00547 cm/cm Grade Count:7 |
| Linear Mold Shrinkage, Transverse | 0.000900 – 0.0100 cm/cm | 0.000900 – 0.0100 in/in | Average value: 0.00647 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 50.0 – 120 MPa | 7250 – 17400 psi | Average value: 90.1 MPa Grade Count:8 |
| Tensile Strength, Yield | 65.5 – 119 MPa | 9500 – 17300 psi | Average value: 90.8 MPa Grade Count:9 |
| Elongation at Break | 3.40 – 40.0 % | 3.40 – 40.0 % | Average value: 10.3 % Grade Count:9 |
| Elongation at Yield | 1.30 – 5.10 % | 1.30 – 5.10 % | Average value: 2.79 % Grade Count:7 |
| Flexural Yield Strength | 82.0 – 141 MPa | 11900 – 20500 psi | Average value: 120 MPa Grade Count:9 |
| Flexural Modulus | 2.30 – 9.74 GPa | 334 – 1410 ksi | Average value: 6.64 GPa Grade Count:10 |
| Izod Impact, Notched | 0.267 – 1.33 J/cm | 0.500 – 2.50 ft-lb/in | Average value: 0.634 J/cm Grade Count:8 |
| Izod Impact, Unnotched | 1.65 – 3.74 J/cm | 3.09 – 7.01 ft-lb/in | Average value: 2.55 J/cm Grade Count:7 |
| Falling Dart Impact | 7.34 – 8.81 J | 5.41 – 6.50 ft-lb | Average value: 8.02 J Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.3 – 185 °C | 209 – 365 °F | Average value: 155 °C Grade Count:7 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 – 179 °C | 200 – 354 °F | Average value: 144 °C Grade Count:10 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1000 – 1.00e+17 ohm-cm | 1000 – 1.00e+17 ohm-cm | Average value: 3.33e+16 ohm-cm Grade Count:6 |
| Surface Resistance | 10000 – 1.00e+6 ohm | 10000 – 1.00e+6 ohm | Average value: 505000 ohm Grade Count:5 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 277 – 335 °C | 531 – 635 °F | Average value: 312 °C Grade Count:7 |
| Melt Temperature | 243 – 335 °C | 469 – 635 °F | Average value: 305 °C Grade Count:7 |
| Mold Temperature | 71.1 – 132 °C | 160 – 270 °F | Average value: 103 °C Grade Count:7 |
| Drying Temperature | 104 – 121 °C | 219 – 250 °F | Average value: 113 °C Grade Count:7 |
| Moisture Content | 0.0200 % | 0.0200 % | Average value: 0.0200 % Grade Count:7 |
| Vent Depth | 0.00380 – 0.00510 cm | 0.00150 – 0.00201 in | Average value: 0.00445 cm Grade Count:5 |