Overview of materials for PVC, 20% Glass Fiber Reinforced
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “PVC, 20% Glass Fiber Reinforced”. Specific grades with glass content between 15% and 24% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 – 1.55 g/cc | 0.0542 – 0.0560 lb/in³ | Average value: 1.52 g/cc Grade Count:4 |
| Linear Mold Shrinkage | 0.000 – 0.0150 cm/cm | 0.000 – 0.0150 in/in | Average value: 0.00533 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83.0 – 85.0 | 83.0 – 85.0 | Average value: 83.8 Grade Count:4 |
| Modulus of Elasticity | 6.55 – 7.03 GPa | 950 – 1020 ksi | Average value: 6.76 GPa Grade Count:4 |
| Flexural Yield Strength | 96.1 – 138 MPa | 13900 – 20000 psi | Average value: 110 MPa Grade Count:4 |
| Flexural Modulus | 6.20 – 6.43 GPa | 899 – 933 ksi | Average value: 6.26 GPa Grade Count:4 |
| Poissons Ratio | 0.410 – 0.420 | 0.410 – 0.420 | Average value: 0.417 Grade Count:3 |
| Shear Modulus | 2.31 – 2.43 GPa | 335 – 352 ksi | Average value: 2.35 GPa Grade Count:3 |
| Izod Impact, Notched | 0.160 – 0.907 J/cm | 0.300 – 1.70 ft-lb/in | Average value: 0.527 J/cm Grade Count:4 |
| Izod Impact, Unnotched | 3.20 – 5.30 J/cm | 5.99 – 9.93 ft-lb/in | Average value: 4.26 J/cm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 27.0 – 31.0 µm/m-°C | 15.0 – 17.2 µin/in-°F | Average value: 28.5 µm/m-°C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.8 – 77.2 °C | 163 – 171 °F | Average value: 75.3 °C Grade Count:4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 – 210 °C | 370 – 410 °F | Average value: 200 °C Grade Count:4 |