Overview of materials for Thermoplastic Polyimide, Unfilled
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 – 1.34 g/cc | 0.0437 – 0.0484 lb/in³ | Average value: 1.29 g/cc Grade Count:8 |
| Linear Mold Shrinkage | 0.00830 – 0.0120 cm/cm | 0.00830 – 0.0120 in/in | Average value: 0.00953 cm/cm Grade Count:3 |
| Melt Flow | 1.21 – 24.2 g/10 min | 1.21 – 24.2 g/10 min | Average value: 9.36 g/10 min Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 58.6 – 92.2 MPa | 8500 – 13400 psi | Average value: 80.9 MPa Grade Count:7 |
| 57.9 – 57.9 MPa
@Temperature 150 – 150 °C
|
8400 – 8400 psi
@Temperature 302 – 302 °F
|
Average value: 57.9 MPa Grade Count:1 | |
| Tensile Strength, Yield | 57.916 – 57.916 MPa
@Temperature 149 – 149 °C
|
8400.0 – 8400.0 psi
@Temperature 300 – 300 °F
|
Average value: 57.9 MPa Grade Count:1 |
| Elongation at Break | 1.80 – 90.0 % | 1.80 – 90.0 % | Average value: 17.0 % Grade Count:7 |
| 90.0 – 90.0 %
@Temperature 150 – 150 °C
|
90.0 – 90.0 %
@Temperature 302 – 302 °F
|
Average value: 90.0 % Grade Count:1 | |
| Elongation at Yield | 90.0 – 90.0 %
@Temperature 149 – 149 °C
|
90.0 – 90.0 %
@Temperature 300 – 300 °F
|
Average value: 90.0 % Grade Count:1 |
| Modulus of Elasticity | 2.41 – 4.50 GPa | 350 – 653 ksi | Average value: 3.73 GPa Grade Count:7 |
| Flexural Yield Strength | 77.2 – 137 MPa | 11200 – 19900 psi | Average value: 110 MPa Grade Count:5 |
| 88.2529 – 88.3 MPa
@Temperature 149 – 150 °C
|
12800.0 – 12800 psi
@Temperature 300 – 302 °F
|
Average value: 88.3 MPa Grade Count:2 | |
| Flexural Modulus | 2.94 – 3.79 GPa | 426 – 550 ksi | Average value: 3.27 GPa Grade Count:5 |
| 2.55 – 2.55037 GPa
@Temperature 149 – 150 °C
|
370 – 369.906 ksi
@Temperature 300 – 302 °F
|
Average value: 2.55 GPa Grade Count:2 | |
| Compressive Yield Strength | 76.4919 – 76.5318 MPa
@Temperature 149 – 150 °C
|
11094.2 – 11100.0 psi
@Temperature 300 – 302 °F
|
Average value: 76.5 MPa Grade Count:2 |
| Shear Strength | 78.5 – 78.5 MPa
@Temperature 150 – 150 °C
|
11400 – 11400 psi
@Temperature 302 – 302 °F
|
Average value: 78.5 MPa Grade Count:1 |
| Izod Impact, Notched | 0.883 – 1.12 J/cm | 1.65 – 2.10 ft-lb/in | Average value: 0.970 J/cm Grade Count:3 |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | Average value: 2.00 J/cm² Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 54.0 – 55.0 µm/m-°C
@Temperature 73.0 – 200 °C
|
30.0 – 30.6 µin/in-°F
@Temperature 163 – 392 °F
|
Average value: 54.5 µm/m-°C Grade Count:2 |
| CTE, linear, Transverse to Flow | 55.0 – 55.0 µm/m-°C
@Temperature 200 – 200 °C
|
30.6 – 30.6 µin/in-°F
@Temperature 392 – 392 °F
|
Average value: 55.0 µm/m-°C Grade Count:1 |
| Specific Heat Capacity | 1.00 – 1.42256 J/g-°C
@Temperature 100 – 300 °C
|
0.239 – 0.340000 BTU/lb-°F
@Temperature 212 – 572 °F
|
Average value: 1.21 J/g-°C Grade Count:2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 – 252 °C | 293 – 485 °F | Average value: 200 °C Grade Count:4 |
| Vicat Softening Point | 130 – 170 °C | 266 – 338 °F | Average value: 150 °C Grade Count:3 |
| Flammability, UL94 | HB – 5VA | HB – 5VA | Grade Count:5 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.51 – 1.54 | 1.51 – 1.54 | Average value: 1.53 Grade Count:3 |
| Transmission, Visible | 90.0 % | 90.0 % | Average value: 90.0 % Grade Count:3 |