Description
Material Notes:
PERMABOND® 735 is a toughened cyanoacrylate with very good impact and peel strength when compared to a conventional cyanoacrylate. It bonds rapidly at room temperature and its viscosity is stable over the shelf life of the product. This provides consistent performance. The product adheres to a variety of surfaces including steel, aluminum, galvanized steel, plastics and elastomers. Features & Benefits: Longer cure allows accurate alignment Toughened and flexible Ease of use – no mixing or heat cure Black – so suitable for dark surfaces 100% reactive, no solvents Information provided by Permabond.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | Uncured |
| Viscosity | 100 – 200 cP
@Temperature 25.0 °C
|
100 – 200 cP
@Temperature 77.0 °F
|
Uncured |
| Storage Temperature | 2.00 – 7.00 °C | 35.6 – 44.6 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | ISO 868 |
| Adhesive Bond Strength | >= 5.00 MPa | >= 725 psi | PC, Substrate Failure, Shear; ISO 4587 |
| >= 6.00 MPa | >= 870 psi | ABS, Substrate Failure, Shear; ISO 4587 | |
| >= 6.00 MPa | >= 870 psi | PVC, Substrate Failure, Shear; ISO 4587 | |
| 13.0 – 15.0 MPa | 1890 – 2180 psi | Aluminum, Shear; ISO 4587 | |
| 24.0 – 30.0 MPa | 3480 – 4350 psi | Steel, Shear; ISO 4587 | |
| Impact | 5.0 – 10 | 5.0 – 10 | kJ/m<sup>2</sup> Adhesive Impact Strength; ASTM D950 |
| Peel Strength | 1.60 – 2.40 kN/m | 9.13 – 13.7 pli | ASTM D903 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | |
| Thermal Conductivity | 0.100 W/m-K | 0.694 BTU-in/hr-ft²-°F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.5
@Frequency 10000 Hz
|
2.5
@Frequency 10000 Hz
|
|
| Dielectric Strength | 25.0 kV/mm | 635 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 0.0833 – 0.167 min | 0.00139 – 0.00278 hour | Phenolic, handling time |
| 0.167 – 0.250 min | 0.00278 – 0.00417 hour | Buna N Rubber, handling time | |
| 0.500 – 0.833 min | 0.00833 – 0.0139 hour | Steel, handling time | |
| 0.583 – 0.833 min | 0.00972 – 0.0139 hour | Aluminum, handling time | |
| 1440 min | 24.0 hour | full strength |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black | Uncured |
| Maximum Gap Fill (mm) | 0.15 | |
| Strength Retention | 10% at 150°C | Relative to 0°C |
| 100% at 0°C | Relative to 0°C | |
| 50% at 100°C | Relative to 0°C | |
| 75% at -50°C | Relative to 0°C | |
| 90% at 50°C | Relative to 0°C |