Plastcom SLOVALEN PC 59 GB 10 PP, 10% glass beads
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
FeaturesCompouded homopolymer PP, with the content of 10% chemically bound glass beads and modifier of mechanical properties. Increased strength in comparison with unfilled PP. Use in all industry sectors. Delivered in the natural mode and in the full RAL colour scale.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Linear Mold Shrinkage | 0.0199 cm/cm | 0.0199 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0202 cm/cm | 0.0202 in/in | |
| Melt Flow | 5.0 g/10 min
@Load 0.325 kg,
Temperature 270 °C |
5.0 g/10 min
@Load 0.716 lb,
Temperature 518 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa | 4350 psi | |
| Elongation at Break | 5.0 % | 5.0 % | |
| Tensile Modulus | 1.50 GPa | 218 ksi | |
| Flexural Strength | 40.0 MPa | 5800 psi | |
| Flexural Modulus | 1.50 GPa | 218 ksi | |
| Charpy Impact Unnotched | 2.00 J/cm²
@Temperature -20.0 °C
|
9.52 ft-lb/in²
@Temperature -4.00 °F
|
|
| 3.00 J/cm²
@Temperature 23.0 °C
|
14.3 ft-lb/in²
@Temperature 73.4 °F
|
||
| Charpy Impact, Notched | 0.300 J/cm²
@Temperature -20.0 °C
|
1.43 ft-lb/in²
@Temperature -4.00 °F
|
|
| 0.600 J/cm²
@Temperature 23.0 °C
|
2.86 ft-lb/in²
@Temperature 73.4 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 150 °C | 302 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | |
| Vicat Softening Point | 100 °C | 212 °F | B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
| Mold Temperature | 30.0 – 50.0 °C | 86.0 – 122 °F | |
| Injection Pressure | 60.0 – 100 MPa | 8700 – 14500 psi |