Plastcom SLOVALEN PC 78 FRT 5 PP, glass fibre, mod. of mech. properties
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
FeaturesModified copolymer PP for injection moulding, contains the modifier of mechanical properties and non halogen and free phosphor flame retardant. Increased strength in comparison with unfilled PP. Applied in all industry branches. Increased strength, toughness, modulus in tension due to the modification. Delivered in natural mode and in the full RAL colour scale.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |
| Linear Mold Shrinkage | 0.0168 cm/cm | 0.0168 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0175 cm/cm | 0.0175 in/in | |
| Melt Flow | 15 g/10 min
@Load 0.325 kg,
Temperature 270 °C |
15 g/10 min
@Load 0.716 lb,
Temperature 518 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 MPa | 2900 psi | |
| Elongation at Break | 3.0 % | 3.0 % | |
| Tensile Modulus | 1.50 GPa | 218 ksi | |
| Flexural Strength | 30.0 MPa | 4350 psi | |
| Flexural Modulus | 1.50 GPa | 218 ksi | |
| Charpy Impact Unnotched | 1.00 J/cm²
@Temperature -20.0 °C
|
4.76 ft-lb/in²
@Temperature -4.00 °F
|
|
| 1.60 J/cm²
@Temperature 23.0 °C
|
7.61 ft-lb/in²
@Temperature 73.4 °F
|
||
| Charpy Impact, Notched | 0.100 J/cm²
@Temperature -20.0 °C
|
0.476 ft-lb/in²
@Temperature -4.00 °F
|
|
| 0.200 J/cm²
@Temperature 23.0 °C
|
0.952 ft-lb/in²
@Temperature 73.4 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 145 °C | 293 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | |
| Vicat Softening Point | 150 °C | 302 °F | B |
| Flammability, UL94 | V-0
@Thickness 1.60 mm
|
V-0
@Thickness 0.0630 in
|
|
| Glow Wire Test | 960 °C | 1760 °F | at 3 mm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
| Mold Temperature | 40.0 – 80.0 °C | 104 – 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
| Injection Pressure | 70.0 – 120 MPa | 10200 – 17400 psi |