Plastcom SLOVALEN PH 49 GF 10 Polypropylene Homopolymer, 10% Glass Fiber
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 10% glass fiber, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP. Applied in all industry branches. Increased strength, toughness, tensile modulus due to the modification. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | STN 64 0111 |
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | STN 64 0808 |
| Linear Mold Shrinkage, Transverse | 0.021 cm/cm | 0.021 in/in | STN 64 0808 |
| Melt Flow | 5.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
5.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | STN EN ISO 527-2 |
| Elongation at Break | 4.0 % | 4.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 3.60 GPa | 522 ksi | STN EN ISO 527-2 |
| Flexural Strength | 60.0 MPa | 8700 psi | STN EN ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 3.00 J/cm²
@Temperature -20.0 °C
|
14.3 ft-lb/in²
@Temperature -4.00 °F
|
STN EN ISO 179 |
| 5.00 J/cm²
@Temperature 23.0 °C
|
23.8 ft-lb/in²
@Temperature 73.4 °F
|
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.100 J/cm²
@Temperature -20.0 °C
|
0.476 ft-lb/in²
@Temperature -4.00 °F
|
STN EN ISO 179 |
| 1.30 J/cm²
@Temperature 23.0 °C
|
6.19 ft-lb/in²
@Temperature 73.4 °F
|
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | DSC; STN EN ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | STN EN ISO 75/A |
| Vicat Softening Point | 130 °C | 266 °F | B; STN EN ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | |
| Injection Pressure | 70.0 – 120 MPa | 10200 – 17400 psi |