Plastcom SLOVALEN PH 49 GF 60 PP reinforced with 60% glass fibre
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Features: Modified homopolymer PP for injection moulding, chemically reinforced with 60% glass fibre, contains the modifier of mechanical properties.Very good strength and tensile modulus. Delivered in natural mode and in the full RAL colour scale.Packaging, transport, stocking: The product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | |
| Linear Mold Shrinkage | 0.0043 cm/cm | 0.0043 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0038 cm/cm | 0.0038 in/in | |
| Melt Flow | 4.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
4.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Tensile Modulus | 12.8 GPa | 1860 ksi | |
| Flexural Strength | 160 MPa | 23200 psi | |
| Flexural Modulus | 10.1 GPa | 1460 ksi | |
| Charpy Impact Unnotched | 4.50 J/cm²
@Temperature -20.0 °C
|
21.4 ft-lb/in²
@Temperature -4.00 °F
|
|
| 4.50 J/cm²
@Temperature 23.0 °C
|
21.4 ft-lb/in²
@Temperature 73.4 °F
|
||
| Charpy Impact, Notched | 0.900 J/cm²
@Temperature -20.0 °C
|
4.28 ft-lb/in²
@Temperature -4.00 °F
|
|
| 1.10 J/cm²
@Temperature 23.0 °C
|
5.23 ft-lb/in²
@Temperature 73.4 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | |
| Vicat Softening Point | 182 °C | 360 °F | |
| Flammability Test | 1.0 | 1.0 | |
| Glow Wire Test | 650 °C | 1200 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 – 270 °C | 464 – 518 °F | |
| Mold Temperature | 70.0 – 90.0 °C | 158 – 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 100 – 140 MPa | 14500 – 20300 psi |