Plastcom SLOVALEN PH 91 GF 10 PP, 10% glass fibre
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 10% glass fibre. Increased strength in comparison with unfilled PP. Applied in all industry branches. Increased strength, toughness, modulus in tension due to the modification. Delivered in natural mode and in the full RAL colour scale.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | |
| Linear Mold Shrinkage, Transverse | 0.021 cm/cm | 0.021 in/in | |
| Melt Flow | 15 g/10 min
@Load 0.325 kg,
Temperature 270 °C |
15 g/10 min
@Load 0.716 lb,
Temperature 518 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | |
| Elongation at Break | 4.0 % | 4.0 % | |
| Tensile Modulus | 3.60 GPa | 522 ksi | |
| Flexural Strength | 60.0 MPa | 8700 psi | |
| Flexural Modulus | 2.40 GPa | 348 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm²
@Temperature -20.0 °C
|
14.3 ft-lb/in²
@Temperature -4.00 °F
|
|
| 5.00 J/cm²
@Temperature 23.0 °C
|
23.8 ft-lb/in²
@Temperature 73.4 °F
|
||
| Charpy Impact, Notched | 0.100 J/cm²
@Temperature -20.0 °C
|
0.476 ft-lb/in²
@Temperature -4.00 °F
|
|
| 1.30 J/cm²
@Temperature 23.0 °C
|
6.19 ft-lb/in²
@Temperature 73.4 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | |
| Vicat Softening Point | 130 °C | 266 °F | B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | |
| Injection Pressure | 70.0 – 120 MPa | 10200 – 17400 psi |