Plastics Group Polifil® GFPPCC-10 10% Glass Reinforced Polypropylene
| Manufacturer | The Plastics Group of America |
| Trade Name | Polifil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polifil® GFPPCC series compounds are homopolymer polypropylenes reinforced with chemically coupled glass fibers. These compounds offer superior strength and stiffness, improved elevated temperature performance, better creep resistance, higher impact strength and higher resistance to high temperature water than conventional glass fiber reinforced polypropylenes.Applications: Chemical resistanceAppliancesElectrical componentsAutomotiveIrrigationUtility productsStandard processing techniques are applicable. Information provided by The Plastics Group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | ASTM D792 |
| Filler Content | 10 % | 10 % | ASTM D2584 |
| Linear Mold Shrinkage | 0.0060 cm/cm
@Thickness 1.59 mm
|
0.0060 in/in
@Thickness 0.0625 in
|
ASTM D955 |
| Melt Flow | 5.0 – 10 g/10 min | 5.0 – 10 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.8 MPa | 7800 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 65.5 MPa | 9500 psi | ASTM D638 |
| Flexural Modulus | 2.69 GPa | 390 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | At 73°F; ASTM D256 |
| Gardner Impact | 0.904 J | 0.667 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |