Plastics Group Polifil® RMC-20V 20% Calcium Carbonate-Reinforced Polypropylene, High Impact, UV Stabilized
| Manufacturer | The Plastics Group of America |
| Trade Name | Polifil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polifil® RMC-V series compounds are high impact, UV stabilized polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, these compounds retard dust and maintain their original state and color for many years.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Filler Content | 20 % | 20 % | ASTM D2584 |
| Linear Mold Shrinkage | 0.012 cm/cm
@Thickness 1.59 mm
|
0.012 in/in
@Thickness 0.0625 in
|
ASTM D955 |
| Melt Flow | 16 – 20 g/10 min | 16 – 20 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 86 | 86 | ASTM D785 |
| Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
| Flexural Modulus | 1.79 GPa | 260 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | At 73°F; ASTM D256 |
| Izod Impact, Unnotched | 12.8 J/cm | 24.0 ft-lb/in | At 73°F; ASTM D256 |
| Gardner Impact | 6.78 J | 5.00 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |