Plenco 1510 Polyester, Granular, Transfer Molded
| Manufacturer | Plenco (Plastics Engineering Company) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PLENCO 01510 is a mineral filled, pelletized polyester molding compound, which offers an excellent combination of electrical properties and dimensional stability. UL recognized under component file E40654. 01510 is available in black.Information supplied by Plenco.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D1895 |
| Density | 2.01 g/cc | 0.0726 lb/in³ | ASTM D792 |
| Water Absorption | 0.133 % | 0.133 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00153 cm/cm | 0.00153 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 78 | 78 | ASTM D785 |
| Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ASTM D638 |
| Elongation at Break | 0.55 % | 0.55 % | ASTM D638 |
| Tensile Modulus | 19.8 GPa | 2870 ksi | ASTM D638 |
| Flexural Strength | 119 MPa | 17300 psi | ASTM D790 |
| Flexural Modulus | 19.9 GPa | 2890 ksi | ASTM D790 |
| Compressive Strength | 194 MPa | 28100 psi | ASTM D695 |
| Poissons Ratio | 0.284 | 0.284 | ASTM D638 |
| Shear Modulus | 7.71 GPa | 1120 ksi | Calculated |
| Izod Impact, Notched | 0.223 J/cm | 0.418 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.274 J/cm² | 1.30 ft-lb/in² | ASTM D256 |
| Impact | 123 | 123 | J/m Drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 54.0 µm/m-°C
@Temperature 40.0 – 130 °C
|
30.0 µin/in-°F
@Temperature 104 – 266 °F
|
TMA; ASTM E831 |
| Thermal Conductivity | 0.730 W/m-K
@Temperature 100 °C
|
5.07 BTU-in/hr-ft²-°F
@Temperature 212 °F
|
ASTM E1461 |
| Maximum Service Temperature, Air | 213 °C | 415 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 251 °C | 484 °F | ASTM D648 |
| Flammability, UL94 | HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
|
| Oxygen Index | 25.5 % | 25.5 % | ASTM D2863 |
| Shrinkage | 0.0167 % | 0.0167 % | 72 hr, 120ºC; ASTM D1299 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.60e+15 ohm-cm | 2.60e+15 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.7 | 4.7 | ASTM D150 |
| Dielectric Strength | 11.8 kV/mm | 300 kV/in | Step by Step; ASTM D149 |
| 15.5 kV/mm | 394 kV/in | Short Time; ASTM D149 | |
| Dielectric Breakdown | 23000 V | 23000 V | 1hr 120C; ASTM D149 |
| Dissipation Factor | 0.0149 | 0.0149 | ASTM D150 |
| Arc Resistance | 192 sec | 192 sec | ASTM D495 |
| Comparative Tracking Index | 600 V | 600 V | ASTM D3638 |