Polykemi AB POLYfill PPHC T20050 Polypropylene, Mineral Reinforced
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Filler Content | 50 % | 50 % | ±2%; Polykemi |
| Melt Index of Compound | 20 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
20 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 25.0 MPa | <= 3630 psi | ISO/R527 |
| Flexural Strength | <= 56.0 MPa | <= 8120 psi | ISO 178 |
| Flexural Modulus | 3.10 GPa
@Temperature 23.0 °C
|
450 ksi
@Temperature 73.4 °F
|
ISO 178 |
| Charpy Impact, Notched | 0.200 J/cm²
@Temperature 23.0 °C
|
0.952 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 86.0 °C
@Load 5.001 kg
|
187 °F
@Load 11.03 lb
|
50°C/h; ISO 306 |
| 145 °C
@Load 1.00 kg
|
293 °F
@Load 2.21 lb
|
50°C/h; ISO 306 | |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
|
| Glow Wire Test | 750 °C
@Thickness 2.00 mm
|
1380 °F
@Thickness 0.0787 in
|
IEC 695-2-1 |