PolyOne Edgetek® QT-20MN/000 natural HI Syndiotactic Polystyrene (SPS)

Manufacturer PolyOne Corporation
Trade Name Edgetek®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union

Description

Material Notes:
Information provided by PolyOne
Physical Properties Metric English Comments
Density 1.20 g/cc

@Temperature 23.0 °C
0.0434 lb/in³

@Temperature 73.4 °F
ISO 1183
Linear Mold Shrinkage, Flow <= 0.013 cm/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
<= 0.013 in/in

@Thickness 0.157 in,
Temperature 73.4 °F
Injection Molded, Bergmann Method; No Standard
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133

 

Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa

@Temperature 23.0 °C
7250 psi

@Temperature 73.4 °F
Type I, 5.0 mm/min; ISO 527
Elongation at Break 1.5 %

@Temperature 23.0 °C
1.5 %

@Temperature 73.4 °F
Type I, 5.0 mm/min; ISO 527
Tensile Modulus 4.20 GPa

@Temperature 23.0 °C
609 ksi

@Temperature 73.4 °F
Type I, 5.0 mm/min; ISO 527
Charpy Impact Unnotched 1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
ISO 179

 

Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 230 °C

@Thickness 3.18 mm
446 °F

@Thickness 0.125 in
Unannealed; ISO 75-2/A
Flammability, UL94 HB

HB

UL 94

 

Processing Properties Metric English Comments
Melt Temperature 270 – 320 °C

518 – 608 °F

Mold Temperature 80.0 – 150 °C

176 – 302 °F

Drying Temperature 80.0 °C

176 °F

Dry Time 2.00 hour

2.00 hour

 

Descriptive Properties Value Comments
Appearance Natural Color

Filler / Reinforcement MineralInorganic

Forms Pellets

Generic Material SPS

Generic Name Syndiotactic Polystyrene (SPS)

Regional Availability Africa & Middle East

Asia Pacific

Europe

North America

South America