PolyOne Stat-Tech™ RA-06CF-09GF/000 Polyarylsulfone – 9% Glass Fiber – 6% Carbon Fiber Reinforced – ESD Applications &a
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 |
| Water Absorption | 0.38 % | 0.38 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm
@Thickness 3.17 mm
|
0.0020 in/in
@Thickness 0.125 in
|
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 98 | 98 | ASTM D785 |
| Tensile Strength, Ultimate | 131 MPa | 19000 psi | ASTM D638 |
| Elongation at Break | 3.0 – 4.0 % | 3.0 – 4.0 % | ASTM D638 |
| Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm
@Thickness 6.35 mm
|
1.20 ft-lb/in
@Thickness 0.250 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 39.6 µm/m-°C
@Temperature 20.0 °C
|
22.0 µin/in-°F
@Temperature 68.0 °F
|
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | CTi Test V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+6 – 1.00e+10 ohm | 1.00e+6 – 1.00e+10 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 343 – 377 °C | 649 – 711 °F | Stock |
| Mold Temperature | 121 – 149 °C | 250 – 300 °F | |
| Drying Temperature | 135 °C | 275 °F |