Polyram RamOfin PPH343T4BK11 Polypropylene, 20% Mineral Filled
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
20% Mineral filled, UV stabilized, heat resistant polypropylene for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.011 – 0.015 cm/cm | 0.011 – 0.015 in/in | ISO 2577 |
| Melt Flow | 10 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
10 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527 |
| Elongation at Break | 25 % | 25 % | ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527 |
| Flexural Strength | 55.0 MPa | 7980 psi | ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 |
| Izod Impact, Unnotched (ISO) | 51.0 kJ/m² | 24.3 ft-lb/in² | ISO 180 |
| Charpy Impact, Notched | 0.280 J/cm² | 1.33 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 168 °C | 334 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ISO 75 |
| Flammability, UL94 | HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
|
| Flame Spread | 22.1 mm/min | 0.870 in/min | FMVSS302 |