Premix Thermoplastics PRE-ELEC® PP 1392 Carbon Black Filled Conductive Thermoplastic Compound
| Manufacturer | Premix Thermoplastics Inc. |
| Trade Name | PRE-ELEC® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PRE-ELEC® PP 1392 is a carbon black filled conductive thermoplastic compound based on polypropylene. In addition to a low electrical resistivity PRE-ELEC® PP 1392 has an excellent balance of mechanical properties and is easy to injection mould. Applications: Injection moulded ESD products such as crates, boxes and tote bins for electronic components.Processing: PRE-ELEC® PP 1392 compound can be processed in the injection moulding machines using normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | |
| Thickness | 102 microns | 4.00 mil | |
| Linear Mold Shrinkage | 0.012 – 0.014 cm/cm | 0.012 – 0.014 in/in | ISO 294-4 |
| Melt Flow | 7.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
7.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| 35 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
35 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 97 | 97 | ISO 868 |
| Hardness, Shore D | 72 | 72 | ISO 868 |
| Tensile Strength | 27.0 MPa | 3920 psi | ISO 527 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ISO 527 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO 527 |
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m²
@Thickness 4.00 mm,
Temperature -20.0 °C |
7.14 ft-lb/in²
@Thickness 0.157 in,
Temperature -4.00 °F |
ISO 180 |
| 32.0 kJ/m²
@Thickness 4.00 mm,
Temperature 23.0 °C |
15.2 ft-lb/in²
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 | |
| Izod Impact, Unnotched (ISO) | NB
@Thickness 4.00 mm,
Temperature 23.0 °C |
NB
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 |
| NB
@Thickness 4.00 mm,
Temperature -20.0 °C |
NB
@Thickness 0.157 in,
Temperature -4.00 °F |
ISO 180 | |
| Charpy Impact Unnotched | NB
@Thickness 102 mm,
Temperature 23.0 °C |
NB
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 |
| NB
@Thickness 102 mm,
Temperature -20.0 °C |
NB
@Thickness 4.00 in,
Temperature -4.00 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.40 J/cm²
@Thickness 102 mm,
Temperature -20.0 °C |
6.66 ft-lb/in²
@Thickness 4.00 in,
Temperature -4.00 °F |
ISO 179 |
| 1.50 J/cm²
@Thickness 102 mm,
Temperature 23.0 °C |
7.14 ft-lb/in²
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | 75/Method Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | 75/Method Af |
| Vicat Softening Point | 88.0 °C | 190 °F | ISO 306/B50 |
| 155 °C | 311 °F | ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 1000 ohm-cm | <= 1000 ohm-cm | ISO D-257 |
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | ISO IEC 61340-5-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
| Mold Temperature | 60.0 – 80.0 °C | 140 – 176 °F | |
| Drying Temperature | 60.0 – 80.0 °C | 140 – 176 °F | Pre-drying |
| Dry Time | 2 – 4 hour | 2 – 4 hour | |
| Injection Pressure | 60.0 – 80.0 MPa | 8700 – 11600 psi | |
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | Moderate |