Premix Thermoplastics PRE-ELEC® PP 1393 Conductive Thermoplastic Compound
| Manufacturer | Premix Thermoplastics Inc. |
| Trade Name | PRE-ELEC® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PRE-ELEC® PP 1393 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a very low electrical resistivity, PRE-ELEC® PP 1393 has an excellent balance of mechanical properties and it is easy to process. Applications: Injection moulded parts for the automotive, medical and electronics industries where a very low volume resistivity is needed. PRE-ELEC® PP 1393 can also be used as a masterbatch and blended with PP. It can also be used in extrusion applications.Processing: PRE-ELEC® PP 1393 compound can be extruded and injection moulded with machines using normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| Thickness | 102 microns | 4.00 mil | |
| Linear Mold Shrinkage | 0.012 – 0.014 cm/cm | 0.012 – 0.014 in/in | ISO 294-4 |
| Melt Flow | 0.50 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
0.50 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 97 | 97 | ISO 868 |
| Hardness, Shore D | 71 | 71 | ISO 868 |
| Tensile Strength | 25.0 MPa | 3630 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m²
@Thickness 4.00 mm,
Temperature -20.0 °C |
1.90 ft-lb/in²
@Thickness 0.157 in,
Temperature -4.00 °F |
ISO 180 |
| 5.00 kJ/m²
@Thickness 4.00 mm,
Temperature 23.0 °C |
2.38 ft-lb/in²
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 | |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m²
@Thickness 4.00 mm,
Temperature -20.0 °C |
9.52 ft-lb/in²
@Thickness 0.157 in,
Temperature -4.00 °F |
ISO 180 |
| NB
@Thickness 4.00 mm,
Temperature 23.0 °C |
NB
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact Unnotched | NB
@Thickness 102 mm,
Temperature 23.0 °C |
NB
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 |
| NB
@Thickness 102 mm,
Temperature -20.0 °C |
NB
@Thickness 4.00 in,
Temperature -4.00 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.600 J/cm²
@Thickness 102 mm,
Temperature -20.0 °C |
2.86 ft-lb/in²
@Thickness 4.00 in,
Temperature -4.00 °F |
ISO 179 |
| 0.800 J/cm²
@Thickness 102 mm,
Temperature 23.0 °C |
3.81 ft-lb/in²
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | 75/Method Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | 75/Method Af |
| Vicat Softening Point | 80.0 °C | 176 °F | ISO 306/B50 |
| 150 °C | 302 °F | ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 5.0 ohm-cm | <= 5.0 ohm-cm | ISO D-257 |
| Surface Resistance | <= 100 ohm | <= 100 ohm | ISO IEC 61340-5-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 200 °C | 392 °F | Cylinder |
| 220 °C | 428 °F | Die | |
| Zone 2 | 210 °C | 410 °F | Cylinder |
| 220 °C | 428 °F | Die | |
| Zone 3 | 210 °C | 410 °F | Die |
| 210 °C | 410 °F | Cylinder | |
| Zone 4 | 220 °C | 428 °F | Die |
| 220 °C | 428 °F | Cylinder | |
| Zone 5 | 220 °C | 428 °F | Die |
| 220 °C | 428 °F | Cylinder | |
| Melt Temperature | 200 – 260 °C | 392 – 500 °F | |
| Mold Temperature | 60.0 – 80.0 °C | 140 – 176 °F | |
| Roll Temperature | 60.0 °C | 140 °F | 3rd Roll |
| 80.0 °C | 176 °F | 2nd Roll | |
| 90.0 °C | 194 °F | 1st Roll | |
| Drying Temperature | 60.0 – 80.0 °C | 140 – 176 °F | Pre-drying |
| Dry Time | 2 – 4 hour | 2 – 4 hour | |
| Injection Pressure | 60.0 – 80.0 MPa | 8700 – 11600 psi | |
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | Moderate |