Premix Thermoplastics PRE-ELEC® PP 1394 Conductive Thermoplastic Compound
| Manufacturer | Premix Thermoplastics Inc. |
| Trade Name | PRE-ELEC® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PRE-ELEC® PP 1394 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PP 1394 has excellent mechanical properties and is easy to extrude. PRE-ELEC® PP 1394 is recommended to be used in thin co-extrusion applications e.g. in coextruded conductive PP tape, film or sheet.Processing: PRE-ELEC® PP 1394 compound can be extruded in the machines using normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| Thickness | 102 microns | 4.00 mil | |
| Linear Mold Shrinkage | 0.012 – 0.017 cm/cm | 0.012 – 0.017 in/in | ISO 294-4 |
| Melt Flow | 1.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
1.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| 15 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
15 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 98 | 98 | ISO 868 |
| Hardness, Shore D | 73 | 73 | ISO 868 |
| Film Elongation at Break, MD | 5.0 %
@Thickness 0.400 mm
|
5.0 %
@Thickness 0.0157 in
|
ISO 527 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 1.20 kJ/m²
@Thickness 4.00 mm,
Temperature -20.0 °C |
0.571 ft-lb/in²
@Thickness 0.157 in,
Temperature -4.00 °F |
ISO 180 |
| 1.50 kJ/m²
@Thickness 4.00 mm,
Temperature 23.0 °C |
0.714 ft-lb/in²
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 | |
| Izod Impact, Unnotched (ISO) | 9.00 kJ/m²
@Thickness 4.00 mm,
Temperature -20.0 °C |
4.28 ft-lb/in²
@Thickness 0.157 in,
Temperature -4.00 °F |
ISO 180 |
| 16.0 kJ/m²
@Thickness 4.00 mm,
Temperature 23.0 °C |
7.61 ft-lb/in²
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact Unnotched | 0.500 J/cm²
@Thickness 102 mm,
Temperature -20.0 °C |
2.38 ft-lb/in²
@Thickness 4.00 in,
Temperature -4.00 °F |
ISO 179 |
| 1.40 J/cm²
@Thickness 102 mm,
Temperature 23.0 °C |
6.66 ft-lb/in²
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm²
@Thickness 102 mm,
Temperature -20.0 °C |
0.952 ft-lb/in²
@Thickness 4.00 in,
Temperature -4.00 °F |
ISO 179 |
| 0.400 J/cm²
@Thickness 102 mm,
Temperature 23.0 °C |
1.90 ft-lb/in²
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 | |
| Film Tensile Strength at Break, MD | 30.0 MPa
@Thickness 0.400 mm
|
4350 psi
@Thickness 0.0157 in
|
ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | 75/Method Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | 75/Method Af |
| Vicat Softening Point | 156 °C | 313 °F | ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 10 ohm-cm
@Thickness 0.400 mm
|
<= 10 ohm-cm
@Thickness 0.0157 in
|
ISO D-257 |
| Surface Resistance | <= 100 ohm
@Thickness 0.400 mm
|
<= 100 ohm
@Thickness 0.0157 in
|
ISO IEC 61340-5-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 210 °C | 410 °F | Cylinder |
| 230 °C | 446 °F | Die | |
| Zone 2 | 220 °C | 428 °F | Cylinder |
| 230 °C | 446 °F | Die | |
| Zone 3 | 220 °C | 428 °F | Die |
| 220 °C | 428 °F | Cylinder | |
| Zone 4 | 230 °C | 446 °F | Die |
| 230 °C | 446 °F | Cylinder | |
| Zone 5 | 230 °C | 446 °F | Die |
| 230 °C | 446 °F | Cylinder | |
| Roll Temperature | 60.0 °C | 140 °F | 3rd Roll |
| 80.0 °C | 176 °F | 2nd Roll | |
| 90.0 °C | 194 °F | 1st Roll | |
| Drying Temperature | 60.0 – 80.0 °C | 140 – 176 °F | Pre-drying |
| Dry Time | 2 – 4 hour | 2 – 4 hour | |
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions |