Premix Thermoplastics PRE-ELEC® PP 1396 Conductive Thermoplastic Compound
| Manufacturer | Premix Thermoplastics Inc. |
| Trade Name | PRE-ELEC® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PRE-ELEC® PP 1396 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PP 1396 has excellent mechanical properties and is easy to extrude. Applications: Extrusion of conductive PP-tape.Processing: PRE-ELEC® PP 1396 compound can be extruded in the machines using normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| Thickness | 102 microns | 4.00 mil | |
| Linear Mold Shrinkage | 0.012 – 0.017 cm/cm | 0.012 – 0.017 in/in | ISO 294-4 |
| Melt Flow | 3.0 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
3.0 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 98 | 98 | ISO 868 |
| Hardness, Shore D | 73 | 73 | ISO 868 |
| Film Elongation at Break, MD | 4.0 %
@Thickness 0.400 mm
|
4.0 %
@Thickness 0.0157 in
|
ISO 527 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m²
@Thickness 4.00 mm,
Temperature 23.0 °C |
0.952 ft-lb/in²
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m²
@Thickness 4.00 mm,
Temperature 23.0 °C |
8.57 ft-lb/in²
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 |
| Charpy Impact Unnotched | 1.40 J/cm²
@Thickness 102 mm,
Temperature 23.0 °C |
6.66 ft-lb/in²
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 0.300 J/cm²
@Thickness 102 mm,
Temperature 23.0 °C |
1.43 ft-lb/in²
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 |
| Film Tensile Strength at Break, MD | 33.0 MPa
@Thickness 0.400 mm
|
4790 psi
@Thickness 0.0157 in
|
ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | 75/Method Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | 75/Method Af |
| Vicat Softening Point | 155 °C | 311 °F | ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 10 ohm-cm
@Thickness 0.400 mm
|
<= 10 ohm-cm
@Thickness 0.0157 in
|
ISO D-257 |
| Surface Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | 5 x stretched tape; ISO IEC 61340-5-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 250 °C | 482 °F | Die |
| 250 °C | 482 °F | Cylinder | |
| Zone 2 | 250 °C | 482 °F | Die |
| 260 °C | 500 °F | Cylinder | |
| Zone 3 | 250 °C | 482 °F | Die |
| 270 °C | 518 °F | Cylinder | |
| Zone 4 | 250 °C | 482 °F | Die |
| 270 °C | 518 °F | Cylinder | |
| Zone 5 | 250 °C | 482 °F | Die |
| 270 °C | 518 °F | Cylinder | |
| Roll Temperature | 90.0 °C | 194 °F | 1st Roll |
| 100 °C | 212 °F | 2nd Roll | |
| 100 °C | 212 °F | 3rd Roll | |
| Drying Temperature | 60.0 – 80.0 °C | 140 – 176 °F | Pre-drying |
| Dry Time | 2 – 4 hour | 2 – 4 hour | |
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions |