Premix Thermoplastics PRE-ELEC® PP 1399 Dissipative Thermoplastic Compound
| Manufacturer | Premix Thermoplastics Inc. |
| Trade Name | PRE-ELEC® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PRE-ELEC® PP 1399 is a dissipative thermoplastic compound based on polypropylene. The electrical dissipation is achieved by using special conductive carbon black. In addition to stable surface resistance between 104-107 ohms PRE-ELEC® PP 1399 has an excellent balance of mechanical properties and is easy to injection mould. Applications: Injection moulded crates, boxes, pallets and tote bins for electronic, automotive and chemical industry to prevent static charges.Processing: PRE-ELEC® PP 1399 compound can be processed in the injection moulding machines using normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | |
| Thickness | 102 microns | 4.00 mil | |
| Linear Mold Shrinkage | 0.012 – 0.018 cm/cm | 0.012 – 0.018 in/in | ISO 294-4 |
| Melt Flow | 4.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
4.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| 20 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
20 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 96 | 96 | ISO 868 |
| Hardness, Shore D | 71 | 71 | ISO 868 |
| Tensile Strength | 18.0 MPa | 2610 psi | ISO 527 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Elongation at Yield | 10 % | 10 % | ISO 527 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m²
@Thickness 4.00 mm,
Temperature -20.0 °C |
1.43 ft-lb/in²
@Thickness 0.157 in,
Temperature -4.00 °F |
ISO 180 |
| NB
@Thickness 4.00 mm,
Temperature 23.0 °C |
NB
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 | |
| Izod Impact, Unnotched (ISO) | NB
@Thickness 4.00 mm,
Temperature 23.0 °C |
NB
@Thickness 0.157 in,
Temperature 73.4 °F |
ISO 180 |
| NB
@Thickness 4.00 mm,
Temperature -20.0 °C |
NB
@Thickness 0.157 in,
Temperature -4.00 °F |
ISO 180 | |
| Charpy Impact Unnotched | NB
@Thickness 102 mm,
Temperature 23.0 °C |
NB
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 |
| NB
@Thickness 102 mm,
Temperature -20.0 °C |
NB
@Thickness 4.00 in,
Temperature -4.00 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.600 J/cm²
@Thickness 102 mm,
Temperature -20.0 °C |
2.86 ft-lb/in²
@Thickness 4.00 in,
Temperature -4.00 °F |
ISO 179 |
| 4.00 J/cm²
@Thickness 102 mm,
Temperature 23.0 °C |
19.0 ft-lb/in²
@Thickness 4.00 in,
Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C | 181 °F | 75/Method Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | 75/Method Af |
| Vicat Softening Point | 150 °C | 302 °F | ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 – 1.00e+7 ohm-cm | 1000 – 1.00e+7 ohm-cm | ISO D-257 |
| Surface Resistance | 10000 – 1.00e+7 ohm | 10000 – 1.00e+7 ohm | ISO IEC 61340-5-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 260 °C | 392 – 500 °F | |
| Mold Temperature | 60.0 – 80.0 °C | 140 – 176 °F | |
| Drying Temperature | 60.0 – 80.0 °C | 140 – 176 °F | Pre-drying |
| Dry Time | 2 – 4 hour | 2 – 4 hour | |
| Injection Pressure | 60.0 – 80.0 MPa | 8700 – 11600 psi | |
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | Moderate |