SABIC Innovative Plastics Geloy CR7520 ASA (Europe-Africa-Middle East)
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Geloy CR7520 is a general purpose injection moulding grade, blend of ASA/SAN. It can be positioned for outside parts in various markets, such as telecommunication, transportation, B&C, lighting and ID.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.55 %
@Temperature 23.0 °C
|
0.55 %
@Temperature 73.4 °F
|
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 – 0.0070 cm/cm | 0.0040 – 0.0070 in/in | on tensile bar; SABIC Method |
| Melt Flow | 7.0 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
7.0 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 8.0 g/10 min
@Load 5.00 kg,
Temperature 260 °C |
8.0 g/10 min
@Load 11.0 lb,
Temperature 500 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ISO 2039-2 |
| Hardness, H358/30 | 70.0 MPa | 10200 psi | ISO 2039-1 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | 5 mm/min; ISO 527 |
| 30.0 MPa | 4350 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | 5 mm/min; ISO 527 |
| 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 10 % | 10 % | 50 mm/min; ISO 527 |
| 15 % | 15 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 1.90 GPa | 276 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 50.0 MPa | 7250 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m²
@Temperature -30.0 °C
|
2.38 ft-lb/in²
@Temperature -22.0 °F
|
80*10*4; ISO 180/1A |
| 9.00 kJ/m²
@Temperature 23.0 °C
|
4.28 ft-lb/in²
@Temperature 73.4 °F
|
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.400 J/cm²
@Temperature -30.0 °C
|
1.90 ft-lb/in²
@Temperature -22.0 °F
|
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.900 J/cm²
@Temperature 23.0 °C
|
4.28 ft-lb/in²
@Temperature 73.4 °F
|
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 155
@Load 1.00 kg
|
155
@Load 2.20 lb
|
CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C
@Temperature 23.0 – 60.0 °C
|
50.0 µin/in-°F
@Temperature 73.4 – 140 °F
|
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C
@Temperature 23.0 – 60.0 °C
|
55.6 µin/in-°F
@Temperature 73.4 – 140 °F
|
ISO 11359-2 |
| Thermal Conductivity | 0.210 W/m-K | 1.46 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 85.0 °C | 185 °F | Rate B/50; ISO 306 |
| 90.0 °C | 194 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB
@Thickness 1.00 mm
|
HB
@Thickness 0.0394 in
|
UL 94 |
| HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
2nd value; UL 94 | |
| Oxygen Index | 19 % | 19 % | LOI; ISO 4589 |
| Glow Wire Test | 750 °C
@Thickness 3.20 mm
|
1380 °F
@Thickness 0.126 in
|
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.2
@Frequency 1.00e+6 Hz
|
3.2
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| 5.2
@Frequency 50.0 – 60.0 Hz
|
5.2
@Frequency 50.0 – 60.0 Hz
|
IEC 60250 | |
| Dielectric Strength | 16.0 kV/mm
@Thickness 3.20 mm
|
406 kV/in
@Thickness 0.126 in
|
in oil; IEC 60243-1 |
| Dissipation Factor | 0.026
@Frequency 1.00e+6 Hz
|
0.026
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| 0.15
@Frequency 50.0 – 60.0 Hz
|
0.15
@Frequency 50.0 – 60.0 Hz
|
IEC 60250 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |