SABIC Innovative Plastics Geloy FXTW26SK ASA (Asia Pacific)
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D 792 |
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 %
@Temperature 23.0 °C
|
0.50 %
@Temperature 73.4 °F
|
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 – 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0040 – 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 – 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0040 – 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| Melt Flow | 12 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
12 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ASTM D 1238 |
| 13 g/10 min
@Load 5.00 kg,
Temperature 260 °C |
13 g/10 min
@Load 11.0 lb,
Temperature 500 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D 638 |
| 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 | |
| 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | Type I, 5 mm/min; ASTM D 638 |
| 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 | |
| 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 17 % | 17 % | Type I, 50 mm/min; ASTM D 638 |
| 18 % | 18 % | Type I, 5 mm/min; ASTM D 638 | |
| 24 % | 24 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D 638 |
| 2.7 % | 2.7 % | Type I, 50 mm/min; ASTM D 638 | |
| 2.8 % | 2.8 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.45 GPa | 355 ksi | 1 mm/min; ISO 527 |
| 2.46 GPa | 357 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 64.0 MPa | 9280 psi | 2 mm/min; ISO 178 |
| 74.0 MPa | 10700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| 2.57 GPa | 373 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.230 J/cm
@Temperature -30.0 °C
|
0.431 ft-lb/in
@Temperature -22.0 °F
|
ASTM D 256 |
| 1.40 J/cm
@Temperature 23.0 °C
|
2.62 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 2.00 kJ/m²
@Temperature -30.0 °C
|
0.952 ft-lb/in²
@Temperature -22.0 °F
|
80*10*4; ISO 180/1A |
| 10.0 kJ/m²
@Temperature 23.0 °C
|
4.76 ft-lb/in²
@Temperature 73.4 °F
|
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.800 J/cm²
@Temperature 23.0 °C
|
3.81 ft-lb/in²
@Temperature 73.4 °F
|
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 18.0 J
@Temperature 23.0 °C
|
13.3 ft-lb
@Temperature 73.4 °F
|
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 83.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
46.1 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 |
| 84.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
46.7 µin/in-°F
@Temperature -40.0 – 104 °F
|
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 94.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
52.2 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 |
| 94.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
52.2 µin/in-°F
@Temperature -40.0 – 104 °F
|
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C
@Thickness 3.20 mm
|
207 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 84.0 °C
@Thickness 3.20 mm
|
183 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| Vicat Softening Point | 95.0 °C | 203 °F | Rate B/50; ISO 306 |
| 98.0 °C | 208 °F | Rate B/50; ASTM D 1525 | |
| 99.0 °C | 210 °F | Rate B/120; ISO 306 |