SABIC Innovative Plastics Geloy XTWM200 ASA (Asia Pacific)
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
ASA resin for injection molding. Excellent flow, colorability and outdoor weathering capability.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D 792 |
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.55 %
@Temperature 23.0 °C
|
0.55 %
@Temperature 73.4 °F
|
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 – 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0040 – 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 – 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0040 – 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| Melt Flow | 12 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
12 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 13.3 g/10 min
@Load 3.80 kg,
Temperature 280 °C |
13.3 g/10 min
@Load 8.38 lb,
Temperature 536 °F |
ASTM D 1238 | |
| 15 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
15 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ASTM D 1238 | |
| 18 g/10 min
@Load 5.00 kg,
Temperature 260 °C |
18 g/10 min
@Load 11.0 lb,
Temperature 500 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM D 785 |
| Tensile Strength at Break | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
| 35.0 MPa | 5080 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 20 % | 20 % | Type I, 50 mm/min; ASTM D 638 |
| 28 % | 28 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 2.8 % | 2.8 % | Type I, 50 mm/min; ASTM D 638 |
| 2.8 % | 2.8 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.39 GPa | 347 ksi | 5 mm/min; ASTM D 638 |
| 2.52 GPa | 365 ksi | 50 mm/min; ASTM D 638 | |
| 2.70 GPa | 392 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 72.0 MPa | 10400 psi | 2 mm/min; ISO 178 |
| 75.0 MPa | 10900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.45 GPa | 355 ksi | 2 mm/min; ISO 178 |
| 2.57 GPa | 373 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.240 J/cm
@Temperature -30.0 °C
|
0.450 ft-lb/in
@Temperature -22.0 °F
|
ASTM D 256 |
| 0.650 J/cm
@Temperature 23.0 °C
|
1.22 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 3.00 kJ/m²
@Temperature -30.0 °C
|
1.43 ft-lb/in²
@Temperature -22.0 °F
|
80*10*4; ISO 180/1A |
| 9.00 kJ/m²
@Temperature 23.0 °C
|
4.28 ft-lb/in²
@Temperature 73.4 °F
|
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.00 J/cm²
@Temperature 23.0 °C
|
4.76 ft-lb/in²
@Temperature 73.4 °F
|
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 3.00 J
@Temperature -30.0 °C
|
2.21 ft-lb
@Temperature -22.0 °F
|
Instrumented Impact Total Energy; ASTM D 3763 |
| 40.0 J
@Temperature 23.0 °C
|
29.5 ft-lb
@Temperature 73.4 °F
|
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 88.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
48.9 µin/in-°F
@Temperature -40.0 – 104 °F
|
ASTM E 831 |
| 88.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
48.9 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 95.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
52.8 µin/in-°F
@Temperature -40.0 – 104 °F
|
ASTM E 831 |
| 95.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
52.8 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 86.0 °C
@Thickness 3.20 mm
|
187 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 77.0 °C
@Thickness 3.20 mm
|
171 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| Vicat Softening Point | 88.0 °C | 190 °F | Rate B/50; ISO 306 |
| 93.0 °C | 199 °F | Rate B/120; ISO 306 | |
| 95.0 °C | 203 °F | Rate B/50; ASTM D 1525 | |
| Flammability, UL94 | HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 94 % | 94 % | untextured, 60 degrees; ASTM D 523 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | NA | IEC 60695-10-2 |
| UV-light, water exposure/immersion | F1 | UL 746C |